Optical laminate, method of producing optical laminate, optical element, and image display

ABSTRACT

The present invention is intended to provide an optical laminate that achieves a superior film strength and a property that a void-provided layer and a pressure-sensitive adhesive/adhesive layer are not easily peeled from each other. The optical laminate of the present invention includes: a void-provided layer; an intermediate layer; and a pressure-sensitive adhesive/adhesive layer, wherein the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked in this order, and the intermediate layer is formed by forming the pressure-sensitive adhesive/adhesive layer on the void-provided layer.

TECHNICAL FIELD

The present invention relates to an optical laminate, a method of producing an optical laminate, an optical element, an image display, a method of producing an optical element, and a method of producing an image display.

BACKGROUND ART

Disposing two substrates at a regular spacing forms an air layer which is a void space between the substrates. The air layer formed between the substrates serves as a low refractive layer that reflects light entirely, for example. Thus, for example, in the case of an optical film, components such as a prism, a polarizing film, and a polarizing plate are disposed at regular spacings to provide air layers each of which serves as a low refractive index layer between the components. Forming air layers in such a manner, however, requires disposing the components at regular spacings, which prevents the components from being stacked sequentially and causes time and trouble in production. Combining optical elements thorough a spacer (frame) or the like for maintaining an air layer increases the thickness of the whole film, which goes against the need for a thin and lightweight film.

For solving such problems, there are attempts to develop a member such as a film having a low refractive index as a substitute for an air layer which is a void space between the components.

An optical element such as a film or the like is generally used as a laminate structure in which the optical element is bonded to a pressure-sensitive adhesive layer or an adhesive layer (hereinafter, also collectively referred to as a “pressure-sensitive adhesive/adhesive layer”). Thus, for example, a laminate of an organic-inorganic composite film with void spaces and a connection layer containing a pressure-sensitive adhesive or an adhesive has been proposed (Patent Document 1).

CITATION LIST Patent Document(s)

Patent Document 1: JP 2014-46518 A

BRIEF SUMMARY OF THE INVENTION Problem to be Solved by the Invention

A conventional layer with void spaces (hereinafter, also referred to as a “void-provided layer”), however, had problems that it is insufficient in film strength and is easily peeled from a pressure-sensitive adhesive/adhesive layer (a layer containing a pressure-sensitive adhesive or an adhesive). In particular, achieving both a high strength and a low refractive index was difficult since the proportion of void space decreases and the refractive index increases when the film strength is improved by a catalyst or the like in formation of a void-provided layer.

Hence, the present invention is intended to provide an optical laminate, a method of producing an optical laminate, an optical element, an image display, a method of producing an optical element, and a method of producing an image display that achieve a superior film strength and a property that a void-provided layer and a pressure-sensitive adhesive/adhesive layer are not easily peeled from each other.

Means for Solving Problem

In order to achieve the above object, the present invention provides an optical laminate including: a void-provided layer; an intermediate layer; and a pressure-sensitive adhesive/adhesive layer, wherein the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked in this order, and the intermediate layer is formed by forming the pressure-sensitive adhesive/adhesive layer on the void-provided layer.

The present invention also provides a method of producing an optical laminate in which a void-provided layer, an intermediate layer, and a pressure-sensitive adhesive/adhesive layer are stacked in this order, including steps of forming the void-provided layer; forming the pressure-sensitive adhesive/adhesive layer on the void-provided layer; and forming the intermediate layer.

The present invention also provides an optical element including: the optical laminate according to the present invention.

The present invention also provides an image display including: the optical element according to the present invention.

The present invention also provides a method of producing an optical element including an optical laminate, wherein the optical element is produced by the method of producing an optical laminate of the present invention.

The present invention also provides a method of producing an image display including an optical element, wherein the optical element is produced by the method of producing an optical element of the present invention.

Effects of the Invention

The optical laminate of the present invention achieves a superior film strength and a property that a void-provided layer and a pressure-sensitive adhesive/adhesive layer are not easily peeled from each other. The production method of an optical laminate of the present invention can produce an optical laminate of the present invention that achieves superior film strength and a property that a void-provided layer and a pressure-sensitive adhesive/adhesive layer are not easily peeled from each other. The optical laminate of the present invention may be, for example, an optical laminate (hereinafter, also referred to as a “laminated film of the present invention”) further including a resin film, wherein the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on the resin film in this order. The present invention, however, is not limited thereto. The optical laminate of the present invention may be used for an optical element and an image display of the present invention, for example. The present invention, however, is not limited thereto and can be used for any purpose.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a process cross sectional view schematically showing an example of the method of forming a void-provided layer 21, an intermediate layer 22, and a pressure-sensitive adhesive/adhesive layer 30 on a resin film 10 in the present invention.

FIG. 2 is an illustration schematically showing an example of a part of the process of producing a rolled laminated film of the present invention (hereinafter, also referred to as “a laminated film roll of the present invention”) and an example of the apparatus used therefore.

FIG. 3 is an illustration schematically showing another example of a part of the process of producing a laminated film roll of the present invention and another example of the apparatus used therefore.

FIG. 4A is a cross sectional photograph of a laminated film produced in Example 1.

FIG. 4B is a cross sectional photograph of a laminated film produced in Example 7.

DETAILED DESCRIPTION OF THE INVENTION

In the optical laminate of the present invention, for example, the thickness of the void-provided layer may be in the range from 0.01 μm to 1000 μm. In the optical laminate of the present invention, for example, the thickness of the intermediate layer may be in the range from 0.001 μm to 10 μm.

In the optical laminate of the present invention, for example, the refractive index of the void-provided layer is 1.25 or less.

In the optical laminate of the present invention, for example, the thickness of the intermediate layer is less than the thickness of the void-provided layer.

In the optical laminate of the present invention, for example, the void-provided layer has a proportion of void space of 40 vol % or more.

In the optical laminate of the present invention, for example, the haze value of the void-provided layer is less than 5%.

In the optical laminate of the present invention, for example, the void-provided layer may be a porous body in which microporous particles are chemically bonded.

The optical laminate of the present invention may be, as described above, an optical laminate (the laminated film of the present invention) further including a resin film, wherein the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on the resin film in this order, for example. In the laminated film of the present invention, for example, the resin film may be a long resin film and the laminated film may be a long laminated film roll.

In the production method of an optical laminate of the present invention, the optical laminate may be an optical laminate including: a void-provided layer; an intermediate layer; and a pressure-sensitive adhesive/adhesive layer, wherein the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked in this order, and the void-provided layer is formed on the resin film in the void-provided layer forming step.

In the production method of an optical laminate of the present invention, the intermediate layer forming step may be a step of causing a part of the void-provided layer to react with a part of the pressure-sensitive adhesive/adhesive layer to form the intermediate layer after the pressure-sensitive adhesive/adhesive layer forming step.

In the production method of an optical laminate of the present invention, for example, the intermediate layer may be formed by heating the void-provided layer and the pressure-sensitive adhesive/adhesive layer in the intermediate layer forming step.

The production method of an optical laminate of the present invention may further include a step of: forming a void-provided structure which is a precursor of the void-provided layer prior to the void-provided layer forming step, wherein the precursor contains a substance that generates a strength improver that improves a strength of the void-provided layer, the substance is a substance that generates the strength improver by light irradiation or heating, the substance does not generate the strength improver in the precursor forming step, and the substance generates the strength improver by light irradiation or heating in at least one of the void-provided layer forming step and the intermediate layer forming step.

In the production method of an optical laminate of the present invention, the void-provided layer may include a part where one kind or two or more kinds of structural units that form a structure with minute void spaces are chemically bonded directly or indirectly, for example. For example, in the void-provided layer, there may be a part where the structural units are in contact with each another but not chemically bonded, for example. Note that, in the present invention, “the structural units are “indirectly bonded” means that the structural units are bonded through binder components each of which is smaller in amount than the amount of the structural unit. On the other hand, “the structural units are “directly bonded” means that the structural units are bonded one another directly without involving binder components and the like. The bond among the structural units may be a bond through catalysis, for example. The bond among the structural units may include a hydrogen bond or a covalent bond, for example. The structural units may be in the shape of at least one of a particle, fiber, and a plate, for example. Each of the structural unit in the shape of a particle and the structural unit in the shape of a plate may be made of an inorganic matter, for example. The configuration element of the structural unit in the shape of a particle may include at least one element selected from the group consisting of Si, Mg, Al, Ti, Zn, and Zr, for example. The structure (structural unit) in the shape of a particle may be a solid particle or a hollow particle, and specific examples thereof include silicon particles, silicon particles with micropores, silica hollow nanoparticles, and silica hollow nanoballoons. The structural unit in the shape of fiber can be, for example, nanofiber having a nano-sized diameter, and specific examples thereof include cellulose nanofiber and alumina nanofiber. The structural unit in the shape of a plate can be, for example, nanoclay. Specifically, the structural unit in the shape of a plate can be, for example, nano-sized bentonite (for example, Kunipia F [product name]). The structural unit in the shape of fiber may be at least one selected from the group consisting of carbon nanofiber, cellulose nanofiber, alumina nanofiber, chitin nanofiber, chitosan nanofiber, polymer nanofiber, glass nanofiber, and silica nanofiber, for example, although it is not particularly limited. The structural unit may be, for example, a microporous particle. For example, the void-provided layer may be a porous body in which microporous particles are chemically bonded, and the microporous particles may be chemically bonded directly or indirectly in the void-provided layer forming step, for example. In this state, as described, “the microporous particles are indirectly bonded” means that the microporous particles may be bonded through binder components each of which is smaller in amount than the amount of the microporous particle, for example. In the present invention, the shape of the “particle” (for example, the microporous particle) is not limited to particular shapes, and can be, for example, a spherical shape or any other shape. Furthermore, in the present invention, the microporous particle may be, for example, a sol-gel beaded particle, a nanoparticle (hollow nanosilica/nanoballoon particle), nanofiber, and the like as described above. In the production method of an optical laminate of the present invention, the microporous particle is, for example, a silicon compound microporous particle and the porous body is a silicone porous body. The silicon compound microporous particle includes, for example, a pulverized product of a gelled silica compound. Another embodiment of the void-provided layer includes a void-provided layer including fibrous substances such as nanofiber, wherein the fibrous substances are entangled to form a layer with void spaces. The production method of such a void-provided layer is not particularly limited, and is the same as that of the void-provided layer of the porous body in which the microporous particles are chemically bonded. Besides the aforementioned embodiment, as described above, the void-provided layer may be a void-provided layer formed by using hollow nanoparticles and nanoclay or a void-provided layer made by using hollow nanoballoons and magnesium fluoride. These void-provided layers may be void-provided layers made of a single configuration substance or of multiple configuration substances. The void-provided layer may be the layer adopting one of the aforementioned embodiments or the layer adopting more than one of the aforementioned embodiments. The present invention is described below mainly with reference to the void-provided layer of a porous body in which the microporous particles are chemically bonded.

In the production method of an optical laminate of the present invention, for example, the microporous particle is a silicon compound microporous particle and the porous body is a silicone porous body. The silicon compound microporous particle may include a pulverized product of a gelled silica compound, for example.

In the production method of an optical laminate of the present invention, for example, the porous structure of the porous body may have an open-cell structure in which the pore structures are interconnected.

The production method of an optical laminate of the present invention may further include steps of preparing a liquid containing the microporous particles (hereinafter, also referred to as a “microporous particle-containing liquid”); coating the resin film with the liquid; and drying the liquid applied on the resin film, wherein the porous body is formed by chemically bonding the microporous particles in the void-provided layer forming step, for example. Furthermore, for example, the void-provided layer may be formed by chemically bonding the microporous particles by catalysis in the void-provided layer forming step.

In the production method of an optical laminate of the present invention, for example, the catalyst is a base catalyst (basic catalyst), and the microporous particle-containing liquid may contain a base generator that generates a base catalyst by light irradiation or heating. In the void-provided layer forming step, for example, the void-provided layer may be formed by chemically bonding the microporous particles by light irradiation. Furthermore, in the void-provided layer forming step, for example, the void-provided layer may be formed by chemically bonding the microporous particles by heating.

In the production method of an optical laminate of the present invention, for example, the refractive index of the void-provided layer after formation of the intermediate layer may be 0.1 more than the refractive index of the void-provided layer before the formation of the intermediate layer. In the production method of an optical laminate of the present invention, for example, the void-provided layer may be formed so as to have a refractive index of 1.25 or less. In the production method of an optical laminate of the present invention, for example, the void-provided layer may be formed so as to have a proportion of void space of 40 vol % or more. In the production method of an optical laminate of the present invention, for example, the void-provided layer may be formed so as to have a thickness in the range from 0.01 μm to 100 μm. In the production method of an optical laminate of the present invention, for example, the void-provided layer may be formed so as to have a haze value of less than 5%.

The production method of an optical laminate of the present invention may further include a step of causing a crosslinking reaction in the void-provided lay, for example. The crosslinking reaction step may be, for example, a strength improving step of improving the strength of the void-provided layer. In the crosslinking reaction step, for example, a crosslinking reaction accelerator for accelerating the crosslinking reaction may be used or a substance that generates the crosslinking reaction accelerator by light irradiation or heating may be used. The crosslinking reaction accelerator may be, for example, a strength improver for increasing (improving) the strength of the void-provided layer. For example, the optical laminate may be an optical laminate in which the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on a resin film in this order, the void-provided layer is formed on the resin film in the void-provided layer forming step, and the crosslinking reaction step is a step of improving a peel strength of the void-provided layer to the resin film. For example, the intermediate layer forming step may also serve as the crosslinking reaction step.

In the production method of an optical laminate of the present invention, for example, the optical laminate may be an optical laminate in which the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on a long resin film in this order, the void-provided layer may be continuously formed on the long resin film in the void-provided layer forming step, and the pressure-sensitive adhesive/adhesive layer may be continuously formed on the void-provided layer in the pressure-sensitive adhesive/adhesive layer forming step.

The optical laminate of the present invention may be formed by the production method of an optical laminate of the present invention, for example.

The present invention is described below in more detail with reference to illustrative examples. The present invention, however, is not limited or restricted by the following description.

[1. Laminated Film (Optical Laminate)]

The optical laminate of the present invention achieves superior film strength and a property that a void-provided layer and a pressure-sensitive adhesive/adhesive layer are not easily peeled from each other. While the reason (mechanism) for this is unknown, it is presumed that the void-provided layer and the pressure-sensitive adhesive/adhesive layer are not easily peeled from each other owing to the anchoring property (anchor effect) of the intermediate layer, for example. The anchoring property (anchor effect) is a phenomenon (effect) that the interface between the void-provided layer and the intermediate layer is strongly fixed because the intermediate layer is entangled in the void-provided layer in the vicinity of the interface. This reason (mechanism), however, is an example of a presumable reason (mechanism), and does not limit the present invention.

As described above, the optical laminate of the present invention may be, for example, an optical laminate (the laminated film of the present invention) further including a resin film, wherein the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on the resin film in this order. The optical laminate of the present invention, however, is not limited thereto, and may be an optical laminate including no resin film. In the following description, the present invention is mainly described with reference to the laminated film of the present invention (optical laminate including a resin film). Regarding the optical laminate of the present invention including no resin film, reference can be made to the description as to the laminated film of the present invention below, unless otherwise stated. The laminated film of the present invention may be, as described above, a laminated film in the form of a roll (the laminated film roll of the present invention). Apart of the laminated film roll of the present invention may be cut to be used as the laminated film of the present invention, for example. Hereinafter, the “laminated film of the present invention” shall include the laminated film roll of the present invention, unless otherwise stated.

Owing to its superior film strength and property that a void-provided layer and a pressure-sensitive adhesive/adhesive layer are not easily peeled from each other, for example, the laminated film of the present invention can be in the form of a roll (the laminated film roll of the present invention), which brings about advantageous effects such as superior manufacturing efficiency, superior handleability, and the like. Furthermore, owing to its void-provided layer having a high flexibility, for example, the laminated film of the present invention can be produced continuously as a rolled product by being formed on a soft resin film and the obtained roll is easy to handle. The production method of a laminated film of the present invention is not particularly limited, and can be produced by the aforementioned production method of a laminated film of the present invention, for example.

In the laminated film of the present invention, the resin film is not limited to particular resin films, and examples of the resin include thermoplastic resins with superior transparency such as polyethylene terephthalate (PET), acryl, cellulose acetate propionate (CAP), cycloolefin polymer (COP), triacetate (TAC), polyethylene naphthalate (PEN), polyethylene (PE), and polypropylene (PP).

The void-provided layer of the laminated film roll or the laminated film of the present invention (hereinafter, also referred to as a “void-provided layer of the present invention”) may be directly stacked on the resin film or indirectly stacked on the resin film through another layer, for example.

The laminated film of the present invention can be said as, for example, a low refractive material having the above-described properties, including the void-provided layer, the intermediate layer, the pressure-sensitive adhesive/adhesive layer, and the resin film, wherein the void-provided layer is stacked on the resin film.

In the void-provided layer of the present invention, the residual ratio of an abrasion resistance showing a film strength, measured with BEMCOT®, is in the range from 60% to 100%, for example. The void-provided layer of present invention having such film strength is resistant to a physical impact in winding during production and in use, for example. The lower limit of the abrasion resistance is, for example, 60% or more, 80% or more, or 90% or more, the upper limit thereof is, for example, 100% or less, 99% or less, or 98% or less, and the abrasion resistance is, for example, in the range from 60% to 100%, 80% to 99%, or 90% to 98%.

The abrasion resistance can be measured by the following method, for example.

(Evaluation of Abrasion Resistance)

(1) The laminated film of the present invention is cut into a circle having a diameter of 15 mm as a sample, and the sliding test (abrasion resistance test) to the void-provided layer is performed using BEMCOT®. The sliding condition is as follows: weight: 100 g, reciprocation: 10 times.

(2) The abrasion resistance of the void-provided layer after completion of the abrasion resistance test described in the item (1) is visually evaluated. The evaluation criteria are as follows:

0 to 9 scratches; good

10 to 29 scratches; fair, and

30 or more scratches; not good.

The folding endurance of the laminated film roll or the laminated film of the present invention measured by the MIT test is, for example, 100 times or more. The folding endurance shows flexibility, for example. Since the present invention has such flexibility, for example, a superior winding ability in continuous production and a superior handleability in use can be achieved, for example.

The lower limit of the folding endurance is, for example, 100 times or more, 500 times or more, or 1000 times or more, the upper limit of the folding endurance is not particularly limited, and is, for example, 10000 times or less, and the folding endurance is, for example, in the range from 100 to 10000 times, 500 to 10000 times, or 1000 to 10000 times.

Flexibility means deformability of a substance, for example. The folding endurance by the MIT test can be measured, for example, by the method described below.

(Evaluation of Folding Endurance Test)

The void-provided layer (the void-provided layer of the present invention) is cut into a piece having a size of 20 mm×80 mm, then the obtained piece is attached to a MIT folding endurance tester (product of TESTER SANGYO CO., LTD., product name: BE-202), and 1.0 N load is applied thereto. A chuck of R 2.0 mm for holding the void-provided layer is used, application of load is at most 10000 times, and the number of times of application of load at the time of fracture of the void-provided layer is assumed as the folding endurance.

The film density of the void-provided layer of the present invention is not particularly limited, and the lower limit thereof is, for example, 1 g/cm³ or more, 10 g/cm³ or more, 15 g/cm³ or more, the upper limit thereof is, for example, 50 g/cm³ or less, 40 g/cm³ or less, or 30 g/cm³ or less, or 2.1 g/cm³ or less, and the film density is, for example, in the range from 5 to 50 g/cm³, 10 to 40 g/cm³, 15 to 30 g/cm³, or 1 to 2.1 g/cm³. In the void-provided layer of the present invention, the lower limit of the porosity based on the film density is, for example, 50% or more, 70% or more, or 85% or more, the upper limit thereof is, for example, 98% or less or 95% or less, and the porosity is, for example, in the range from 50% to 98%, 70% to 95%, or 85% to 95%.

The film density can be measured, for example, by the method described below, and the porosity can be calculated, for example, as described below based on the film density.

(Evaluation of Film Density and Porosity)

After forming a void-provided layer (the void-provided layer of the present invention) on a base (acrylic film), the X-ray reflectivity in a total reflection region of the void-provided layer of this laminate is measured using an X-ray diffractometer (product of RIGAKU, product name: RINT-2000). Then, after fitting with Intensity at 2θ, the film density (g/cm³) is calculated from the total reflection angle of the laminate (void-provided layer and base), and the porosity (P %) is calculated by the following formula.

porosity (P %) =45.48×film density (g/cm³)+100(%)

The void-provided layer of the present invention has, for example, a pore structure. The size of a void space (pore) in the present invention indicates not the diameter of the short axis but the diameter of the long axis of the void space. The size of a void space (pore) is preferably in the range from 2 nm to 500 nm, for example. The lower limit of the size of a void space is, for example, 2 nm or more, 5 nm or more, 10 nm or more, or 20 nm or more, the upper limit of the size of a void space is, for example, 500 nm or less, 200 nm or less, or 100 nm or less, and the size of a void space is, for example, in the range from 2 nm to 500 nm, 5 nm to 500 nm, 10 nm to 200 nm, or 20 nm to 100 nm. A preferable size of a void space changes depending on applications of the void-provided structure. Thus, the size of a void space should be adjusted to a desired size according to purposes, for example. The size of a void space can be evaluated by the method described below.

(Evaluation of Size of Void Space)

In the present invention, the size of a void space can be quantified according to the BET test. Specifically, 0.1 g of a sample (the void-provided layer of the present invention) is set in the capillary of a surface area measurement apparatus (product of Micromeritics, product name: ASAP 2020), and dried under a reduced pressure at room temperature for 24 hours to remove gas in the void-provided structure. Then, an adsorption isotherm is created by adsorbing a nitrogen gas to the sample, thereby obtaining a pore distribution. The size of a void space can thereby be evaluated.

It is only required that the void-provided layer of the present invention has a pore structure (porous structure) as described above, for example, and the void-provided layer may have an open-cell structure in which the pore structures are interconnected, for example. The open-cell structure means, for example, that the pore structures are three-dimensionally interconnected in the silicon porous body, i.e., void spaces in the pore structures are interconnected. When a porous body has an open-cell structure, the porosity of the bulk body can be increased. However, an open-cell structure cannot be formed with closed-cell particles such as hollow silica. In this regard, for example, when the silica sol particle (pulverized product of a gelled silicon compound which forms sol) is used, since the particles have a three-dimensional dendritic structure, the void-provided layer of the present invention can form an open-cell structure easily by settlement and deposition of the dendritic particles in a coating film (sol coating film containing the pulverized products of a gelled silicon compound). The void-provided layer of the present invention preferably forms a monolith structure in which the open-cell structure has multiple pore distributions. The monolith structure denotes a hierarchical structure including a structure in which nano-sized void spaces are present and an open-cell structure in which the nano-sized spaces are aggregated, for example. The monolith structure can impart a film strength with minute void spaces while imparting a high porosity with coarse open-cell structure, which achieve both a film strength and a high porosity, for example. For forming such a monolith structure, for example, it is preferable to control the pore distribution of a void-provided structure to be created in a gel (gelled silicon compound) before pulverizing into the silica sol particles. For example, by controlling the particle size distribution of silica sol particles after pulverization to a desired size in pulverization of the gelled silicon compound, the monolith structure can be formed.

In the void-provided layer of the present invention, the haze showing transparency is not particularly limited, and the upper limit thereof is, for example, less than 5% or less than 3%, the lower limit thereof is, for example, 0.1% or more or 0.2% or more, and the haze is, for example, 0.1% or more and less than 5% or 0.2% or more and less than 3%.

The haze can be measured, for example, by the method described below.

(Evaluation of Haze)

A void-provided layer (the void-provided layer of the present invention) is cut into a piece having a size of 50 mm×50 mm, and the obtained piece is set to a hazemeter (product of Murakami Color Research Laboratory, product name: HM-150) to measure a haze. The haze value is calculated by the following formula.

haze (%)=[diffuse transmittance (%)/total light transmittance (%)]×100(%)

Commonly, a ratio between the transmission speed of the wavefront of light in vacuum and the phase velocity of light in a medium is called a refractive index of the medium. The upper limit of the refractive index of the void-provided layer of the present invention is, for example, 1.25 or less, 1.20 or less or 1.15 or less, the lower limit thereof is, for example, 1.05 or more, 1.06 or more, or 1.07 or more, and the refractive index is, for example, in the range from 1.05 to 1.20, 1.06 to 1.20, or 1.07 to 1.15.

In the present invention, the refractive index is a refractive index measured at the wavelength of 550 nm unless otherwise stated. The method of measuring a refractive index is not limited to particular methods, and the refractive index can be measured, for example, by the method described below.

(Evaluation of Refractive Index)

After forming a void-provided layer (the void-provided layer of the present invention) on an acrylic film, the obtained laminate is cut into a piece having a size of 50 mm×50 mm, and the obtained piece is adhered on the front surface of a glass plate (thickness: 3 mm) through a pressure-sensitive adhesive layer. The center of the back surface of the glass plate (diameter: about 20 mm) is solidly painted with a black magic marker, thereby preparing a sample which allows no reflection at the back surface of the glass plate. The sample is set to an ellipsometer (product of J. A. Woollam Japan, product name: VASE), the refractive index is measured at the wavelength of 500 nm and at the incidence angle of 50° to 80°, and the average value is assumed as a refractive index.

The peel strength showing adhesion between the void-provided layer of the present invention and the pressure-sensitive adhesive/adhesive layer stacked thereon is not particularly limited, and the lower limit thereof is, for example, 1 N/25 mm or more, 1.3 N/25 mm or more, 1.5 N/25 mm or more, 2 N/25 mm or more, or 3 N/25 mm or more, the upper limit thereof is, for example, 30 N/25 mm or less, 20 N/25 mm or less, or 10 N/25 mm or less, and the peel strength is, for example, in the range from 1 to 30 N/25 mm, 2 to 20 N/25 mm, or 3 to 10 N/25 mm.

The method of measuring the peel strength is not limited to particular methods, and the peel strength can be measured by the method described below, for example.

(Evaluation of Peel Strength)

From the laminated film of the present invention, a piece having a size of 50 mm×140 mm is obtained as a sample and the sample is fixed to a stainless plate with a double-sided tape. An acrylic pressure-sensitive adhesive layer (thickness: 20 μm) is adhered to a PET film (product of Mitsubishi Plastics, Inc., product name: T100), the thus obtained adhesive tape is cut into a piece having a size of 25 mm×100 mm, and the obtained piece is adhered to the laminated film of the present invention on the other side of the resin film to form a laminate of the PET film and the void-provided layer. Then, the sample is chucked in an autograph tensile testing machine (product of Shimadzu Corporation, product name: AG-Xplus) with a chuck space of 100 mm, and the tensile test is performed at the tensile speed of 0.3 m/min. The average of 50 mm peel test is assumed as the peel strength.

The thickness of the void-provided layer of the present invention is not particularly limited, and the lower limit thereof is, for example, 0.01 μm or more, 0.05 μm or more, 0.1 μm or more, or 0.3 μm or more, the upper limit thereof is, for example, 1000 μm or less, 100 μm or less, 80 μm or less, 50 μm or less, or 10 μm or less, and the thickness is, for example, in the range from 0.01 μm to 100 μm.

As described above, the void-provided layer of the present invention includes pulverized products of a gelled compound, wherein the pulverized products are chemically bonded, for example. In the void-provided layer of the present invention, the pattern of the chemical bond among the pulverized products is not limited to particular patterns. Specifically, the chemical bond can be, for example, a crosslinking bond. The method of chemically bonding the pulverized products is described in detail in the description as to the production method of the present invention.

The gel form of the gelled compound is not limited to particular forms. The “gel” commonly denotes a solidified state of solutes aggregated as they lost independent motility due to interaction. Commonly, a wet gel is a gel containing a dispersion medium in which solutes build a uniform structure, and a xerogel is a gel from which a solvent is removed and in which solutes form a network structure with void spaces. In the present invention, the gelled compound can be a wet gel or a xerogel, for example.

The gelled compound can be, for example, a gelled product obtained by gelating monomer compounds. Specifically, the gelled silicon compound can be, for example, a gelled product in which the monomer silicon compounds are bonded. As a specific example, the gelled silicon compound can be a gelled product in which the monomer silicon compounds are bonded by a hydrogen bond or an intermolecular bond. The bond can be, for example, a bond by dehydration condensation. The method of gelation is described below in the description as to the production method of the present invention.

In the void-provided layer of the present invention, the volume average particle size showing particle size variations of the pulverized product is not particularly limited, and the lower limit thereof is, for example, 0.10 μm or more, 0.20 μm or more, or 0.40 μm or more, the upper limit thereof is, for example, 2.00 μm or less, 1.50 μm or less, or 1.00 μm or less, and the volume average particle size is, for example, in the range from 0.10 μm to 2.00 μm, 0.20 μm to 1.50 μm, or 0.40 μm to 1.00 μm. The particle size distribution can be measured, for example, using a particle size distribution analyzer based on dynamic light scattering, laser diffraction, or the like or using an electron microscope such as a scanning electron microscope (SEM) or a transmission electron microscope (TEM).

The particle size distribution showing particle size variations of the pulverized product is not particularly limited. The distribution of the particle having a particle size of 0.4 μm to 1 μm is in the range from 50 wt % to 99.9 wt %, 80 wt % to 99.8 wt %, or 90 wt % to 99.7 wt % or the distribution of the particle having a particle size of 1 μm to 2 μm is in the range from 0.1 wt % to 50 wt %, 0.2 wt % to 20 wt %, or 0.3 wt % to 10 wt %, for example. The particle size distribution can be measured, for example, using a particle size distribution analyzer or an electron microscope.

In the void-provided layer of the present invention, the type of the gelled compound is not limited to particular types. The gelled compound can be, for example, a gelled silicon compound. The present invention is described below with reference to an example in which the gelled compound is a gelled compound. The present invention, however, is not limited thereto.

The crosslinking bond is, for example, a siloxane bond. Examples of the siloxane bond include T2 bond, T3 bond, and T4 bond shown below. In the case where the void-provided layer of the present invention has the siloxane bond, the void-provided layer of the present invention may have one of, two of, or all of the above-mentioned three bond patterns, for example.

The void-provided layer having higher proportions of T2 and T3 is superior in flexibility and can be expected to have an original property of a gel but is inferior in film strength. On the other hand, the void-provided layer having a higher proportion of T4 is superior in film strength but has small sized void spaces and is inferior in flexibility. Thus, it is preferable to change the proportions of T2, T3, and T4 depending on applications, for example.

In the case where the void-provided layer of the present invention has the siloxane bond, the relative ratio among T2, T3, and T4 with T2 being considered as “1” is, for example, as follows: T2:T3:T4=1:[1 to 100]:[to 50], 1:[1 to 80]:[1 to 40], or 1:[5 to 60]:[1 to 30].

The silicon atoms contained in the void-provided layer of the present invention are preferably bonded by a siloxane bond, for example. As a specific example, the proportion of the unbonded silicon atoms (i.e., residual silanol) among all the silicon atoms contained in the void-provided layer is, for example, less than 50%, 30% or less, or 15% or less.

When the gelled compound is the gelled silicon compound, the monomer silicon compound is not limited to particular compounds. The monomer silicon compound can be, for example, a compound represented by the following chemical formula (1). When the gelled silicon compound is a gelled product in which monomer silicon compounds are bonded by a hydrogen bond or an intermolecular bond as described above, monomers in the chemical formula (1) can be bonded by a hydrogen bond through their hydroxyl groups, for example.

In the chemical formula (1), for example, X is 2, 3, or 4, and R¹ represents a linear or a branched alkyl group. The carbon number of R¹ is, for example, 1 to 6, 1 to 4, or 1 to 2. Examples of the linear alkyl group include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, and a hexyl group, and examples of the branched alkyl group include an isopropyl group and an isobutyl group. The X is, for example, 3 or 4.

A specific example of the silicon compound represented by the chemical formula (1) can be a compound represented by the chemical formula (1′), wherein X is 3. In the chemical formula (1′), R¹ is the same as that in the chemical formula (1), and is, for example, a methyl group. When R¹ represents a methyl group, the silicon compound is tris(hydroxy)methylsilane. When X is 3, the silicon compound is, for example, trifunctional silane having three functional groups.

A specific example of the silicon compound represented by the chemical formula (1) can be a compound represented by the chemical formula (1′) wherein X is 4. In this case, the silicon compound is, for example, tetrafunctional silane having four functional groups.

The monomer silicon compound may be, for example, a hydrolysate of a silicon compound precursor. The silicon compound precursor is not limited as long as it can generate the silicon compound by hydrolysis, for example. A specific example of the silicon compound precursor can be a compound represented by the following chemical formula (2).

In the chemical formula (2), for example, X is 2, 3, or 4, R¹ and R² each represent a linear or branched alkyl group, R¹ and R² may be the same or different, R¹ may be the same or different in the case where X is 2, and R² may be the same or different.

X and R¹ are the same as those in the chemical formula (1), for example. Regarding R², for example, reference can be made to the examples of R¹ in the chemical formula (1).

A specific example of the silicon compound precursor represented by the chemical formula (2) can be a compound represented by the chemical formula (2′) wherein X is 3. In the chemical formula (2′), R¹ and R² are the same as those in the chemical formula (2). When R¹ and R² both represent methyl groups, the silicon compound precursor is trimethoxy(methyl)silane (hereinafter, also referred to as “MTMS”).

The monomer silicon compound is preferably the trifunctional silane because it is superior in the lowness of refractive index. Also, the monomer silicon compound is preferably the tetrafunctional silane because it is superior in strength (for example, abrasion resistance). Regarding the monomer silicon compounds which are raw materials of the gelled silicon compound, one of the compounds may be used alone or two or more of them may be used in combination, for example. As a specific example, the monomer silicon compound may include only the trifunctional silane, only the tetrafunctional silane, or both of the trifunctional silane and the tetrafunctional silane, and may further include other silicon compounds, for example. When two or more kinds of silicon compounds are used as the monomer silicon compound, the ratio between the compounds is not particularly limited and can be determined appropriately.

In the laminated film of the present invention, the void-provided layer may contain a catalyst for chemically bonding one kind or two or more kinds of structural units that form a structure with minute void spaces, for example. The content of the catalyst is not particularly limited, and the content of the catalyst relative to the weight of the structural unit is, for example, 0.01 wt % to 20 wt %, 0.05 wt % to 10 wt %, or 0.1 wt % to 5 wt %.

In the laminated film of the present invention, the void-provided layer may further contain a crosslinking assisting agent for indirectly bonding one kind or two or more kinds of structural units that form a structure with minute void spaces, for example. The content of the crosslinking assisting agent is not particularly limited, and the content of the crosslinking assisting agent relative to the weight of the structural unit is, for example, 0.01 wt % to 20 wt %, 0.05 wt % to 15 wt %, or 0.1 wt % to 10 wt %.

In the present invention, the pressure-sensitive adhesive/adhesive layer is not particularly limited. In the present invention, the “pressure-sensitive adhesive/adhesive layer” is, for example, a layer containing at least one of a pressure-sensitive adhesive and an adhesive, and may be, for example, a pressure-sensitive adhesive layer or an adhesive layer. In the present invention, a “pressure-sensitive adhesive” and a “pressure-sensitive adhesive layer” are used based on the premise that an adherend is re-peelable, for example. In the present invention, an “adhesive” and an “adhesive layer” are used based on the premise that an adherend is not re-peelable, for example. In the present invention, however, the “pressure-sensitive adhesive” and the “adhesive” are not always distinguishable and the “pressure-sensitive adhesive layer” and the “adhesive layer” are not always distinguishable. In the present invention, there is no particular limitation on the pressure-sensitive adhesives or the adhesives for forming the pressure-sensitive adhesive/adhesive layer, and a common pressure-sensitive adhesive or adhesive can be used, for example. Examples of the pressure-sensitive adhesive and the adhesive include polymer adhesives such as acrylic adhesives, vinyl alcohol adhesives, silicone adhesives, polyester adhesives, polyurethane adhesives, and polyether adhesives; and rubber adhesives. Furthermore, the pressure-sensitive adhesive and the adhesive can be an adhesive including a water-soluble crosslinking agent of vinyl alcohol polymer such as glutaraldehyde, melamine, or an oxalic acid. One type of the pressure-sensitive adhesives and adhesives may be used alone or two or more types of them may be used in combination (for example, mixing, lamination, and the like). The thickness of the pressure-sensitive adhesive/adhesive layer is not particularly limited, and is, for example, 0.1 to 100 μm, 5 to 50 μm, 10 to 30 μm, or 12 to 25 μm.

In the present invention, the intermediate layer is not particularly limited, and is, for example, a layer formed by causing a part of the void-provided layer to be united with a part of the pressure-sensitive adhesive/adhesive layer as described above. The thickness of the intermediate layer is not particularly limited, and is, for example, 1 nm to 1500 nm, 5 nm to 1000 nm, 10 nm to 800 nm, or 20 nm to 500 nm.

The form of the laminated film of the present invention is not limited to particular forms, and is normally in the form of a film.

The laminated film of the present invention is, for example, a roll. For example, the present invention may further include a resin film, and the void-provided layer may be formed on the long resin film as described above. In this case, another long film may be stacked on the laminated film of the present invention. Specifically, another long resin film (for example, interleaving paper, release film, surface protection film, or the like) may be stacked on the laminated film of the present invention including the resin film and the void-provided layer, and then the obtained laminate may be wound in the form of a roll.

The method of producing a laminated film of the present invention is not limited to particular methods, and the laminated film of the present invention can be produced, for example, by the production method of the present invention described below. The production method of an optical laminate of the present invention including no resin film can be performed in the same manner as the production method of the laminated film of the present invention except that a resin film is not used unless otherwise stated.

[2. Production Method of Laminated Film]

The production method of a laminated film of the present invention is a method of producing a laminated film in which a void-provided layer, an intermediate layer, and a pressure-sensitive adhesive/adhesive layer are stacked in this order and the void-provided layer and the pressure-sensitive adhesive/adhesive layer are bonded through the intermediate layer, including steps of forming the void-provided layer; forming the pressure-sensitive adhesive/adhesive layer on the void-provided layer; and causing the void-provided layer to react with the pressure-sensitive adhesive/adhesive layer to form an intermediate layer.

In the production method of a laminated film of the present invention, as described above, the void-provided layer is a porous body in which microporous particles are chemically bonded, and the microporous particles are chemically bonded in the void-provided layer forming step, for example. The production method of a laminated film of the present invention, as described above, further including steps of; preparing a liquid containing the microporous particles; coating the resin film with the liquid; and drying the liquid applied on the resin film, wherein the porous body is formed by chemically bonding the microporous particles in the void-provided layer forming step, for example. The liquid containing the microporous particles (microporous particle-containing liquid) is not limited to particular liquids, and can be, for example, a suspension containing the microporous particles. The present invention is described below mainly with reference to an example in which the microporous particle is a pulverized product of a gelled compound and the void-provided layer is a porous body (preferably, silicone porous body) including pulverized products of a gelled compound. The present invention, however, can be performed in the same manner also in the case where the microporous particle is something other than the pulverized product of a gelled compound.

The production method of the present invention forms a void-provided layer which is superior in the lowness of refractive index, for example. The following theory about the reason for this can be formed. The present invention, however, is not limited thereto.

Since the pulverized product used in the production method of the present invention is obtained by pulverizing the gelled silicon compound, the three-dimensional structure of the gelled silicon compound before pulverization is dispersed into three-dimensional basic structures. In the production method of the present invention, the precursor having a porous structure based on the three-dimensional basic structures is formed by coating the base with the pulverized products of a gelled silicon compound. That is, according to the production method of the present invention, a new porous structure is formed of the pulverized products each having the three-dimensional basic structure, which is different from the three-dimensional structure of the gelled silicon compound. Thus, the finally obtained void-provided layer brings about an effect of a low refractive index equivalent to an air layer, for example. Moreover, in the production method of the present invention, since the pulverized products are chemically bonded, the new three-dimensional structure is immobilized. Thus, the finally obtained void-provided layer, despite its structure with void spaces, can maintain a sufficient strength and sufficient flexibility. The void-provided layer obtained by the production method of the present invention is useful as a substitute for the air layer, in an aspect of low refractive index as well as in strength and flexibility, for example. In the case of an air layer, the air layer is formed between the components by stacking components with a space by providing a spacer or the like therebetween. The void-provided layer obtained by the production method of the present invention can achieve a low refractive index equivalent to the air layer simply by disposing it at a desired site, for example. Thus, as described above, the present invention can impart a low refractive index equivalent to the air layer to an optical element easier and simpler than forming the air layer.

In the production method of the present invention, as described above, the void-provided layer is caused to react with the pressure-sensitive adhesive/adhesive layer to form the intermediate layer (intermediate layer forming step). Owing to the intermediate layer, the void-provided layer and the pressure-sensitive adhesive/adhesive layer are not easily peeled from each other, for example. While the reason (mechanism) for this is unknown, as described above, it is presumed that the void-provided layer and the pressure-sensitive adhesive/adhesive layer are not easily peeled from each other owing to the anchoring property (anchor effect) of the intermediate layer, for example. The reaction between the void-provided layer and the pressure-sensitive adhesive/adhesive layer is not limited to particular reactions, and can be, for example, a reaction by catalysis. The reaction between the void-provided layer and the pressure-sensitive adhesive/adhesive layer may be, for example, a reaction (for example, crosslinking reaction) that generates a new chemical bond.

As described below, the intermediate layer forming step may also serve as a step of improving the strength of the void-provided layer. While the mechanism that improves the strength of the void-provided layer by the intermediate layer forming step is unknown, for example, the following theories can be formed. That is, in the intermediate layer forming step, for example, the intermediate layer is formed by causing the void-provided layer and the pressure-sensitive adhesive/adhesive layer to react with each other by applying energy by heating or the like. It is considered that the energy such as heating or the like increases the number of crosslinkages (chemical bonds) inside the void-provided layer, thereby improving the strength of the void-provided layer. This reaction proceeds by a catalyst, a crosslinking reaction accelerator, or a strength improver contained in the void-provided layer, for example. As another theory, sol contained in the pressure-sensitive adhesive enters void spaces of the void-provided layer, and the anchoring force of the intermediate layer is improved by the anchor effect. However, these are examples of a presumable mechanism and do not limit the present invention.

In the void-provided layer forming step, for example, the void-provided layer is formed by chemically bonding the microporous particles by catalysis using a photobase generator. It is considered, for example, that since the base catalyst (crosslinking reaction accelerator) generated from the photobase generator remains in the precursor, the chemical bond (for example, crosslinking reaction) among the microporous particles is further promoted by heating in the intermediate layer forming step, thereby improving the strength of the void-provided layer. As a specific example, when the microporous particles are silicon compound microporous particles (for example, pulverized products of a gelled silica compound) and residual silanol groups (OH groups) are present in the void-provided layer, it is considered that the residual silanol groups are chemically bonded by a crosslinking reaction. The description, however, is an illustrative example and does not limit the present invention.

Regarding the production method of the present invention, reference can be made to the description as to the laminated film of the present invention unless otherwise stated.

Regarding the gelled compound, the pulverized product thereof, the monomer compound, and the precursor of the monomer compound in the production method of the present invention, reference can be made to the description as to the void-provided layer of the present invention.

The production method of the laminated film of the present invention can be performed as described below, for example. The present invention, however, is not limited thereto.

The production method of the laminated film of the present invention, for example, includes a step of preparing the microporous particle-containing liquid as described above. When the microporous particle is a pulverized product of a gelled compound, the pulverized product can be obtained, for example, by pulverizing the gelled compound. By pulverization of the gelled compound, as described above, the three-dimensional structure of the gelled compound is destroyed and dispersed into three-dimensional basic structures.

Generation of the gelled compound by gelation of the monomer compound and preparation of the pulverized product by pulverization of the gelled compound are described below with reference to examples. The present invention, however, is not limited thereto.

The gelation of the monomer compound can be performed, for example, by bonding the monomer compounds by a hydrogen bond or an intermolecular bond.

The monomer compound can be, for example, a silicon compound represented by the chemical formula (1) described in the description as to the void-provided layer of the present invention.

Since the silicon compound represented by the chemical formula (1) has a hydroxyl group, monomers in the chemical formula (1) can be bonded by a hydrogen bond or an intermolecular bond through their hydroxyl groups, for example.

The silicon compound may be the hydrolysate of the silicon compound precursor as described above, and may be generated by hydrolyzing the silicon compound precursor represented by the chemical formula (2) described in the description as to the void-provided layer of the present invention, for example.

The method of hydrolyzing the monomer compound precursor is not limited to particular methods, and can be performed by a chemical reaction in the presence of a catalyst, for example. Examples of the catalyst include acids such as an oxalic acid and an acetic acid. The hydrolysis reaction can be performed, for example, by gradually dropping an oxalic acid aqueous solution to a mixture (for example, suspension) of the silicon compound and dimethylsulfoxide to mix at room temperature, and stirring the resultant for about 30 minutes. In hydrolysis of the silicon compound precursor, for example, by completely hydrolyzing the alkoxy group of the silicon compound precursor, gelation and aging thereafter and heating and immobilization after formation of a void-provided structure can be achieved more efficiently.

The gelation of the monomer compound can be performed, for example, by a dehydration condensation reaction among the monomers. The dehydration condensation reaction is preferably performed in the presence of a catalyst, for example. Examples of the catalyst include dehydration condensation catalysts such as: acid catalysts including a hydrochloric acid, an oxalic acid, and a sulfuric acid; and base catalysts including ammonia, potassium hydroxide, sodium hydroxide, and ammonium hydroxide. The dehydration condensation catalyst is particularly preferably a base catalyst. In the dehydration condensation reaction, the amount of the catalyst to be added to the monomer compound is not particularly limited, and is, for example, 0.1 to 10 mol, 0.05 to 7 mol, or 0.1 to 5 mol per mol of the monomer compound.

The gelation of the monomer compound is preferably performed in a solvent, for example. The proportion of the monomer compound in the solvent is not particularly limited. Examples of the solvent include dimethylsulfoxide (DMSO), N-methylpyrrolidone (NMP), N, N-dimethylacetamide (DMAc), dimethylformamide (DMF), γ-butyrolactone (GBL), acetonitrile (MeCN), and ethylene glycol ethyl ether (EGEE). One of the solvents may be used alone or two or more of them may be used in combination, for example. Hereinafter, the solvent used for the gelation is also referred to as a “gelation solvent”.

The condition for the gelation is not limited to particular conditions. Regarding the treatment of the solvent containing the monomer compound, the treatment temperature is, for example, 20° C. to 30° C., 22° C. to 28° C., or 24° C. to 26° C., and the treatment time is, for example, 1 to 60 minutes, 5 to 40 minutes, or 10 to 30 minutes. The treatment condition for the dehydration condensation reaction is not limited to particular conditions, and reference can be made to these examples. By gelation, a siloxane bond is grown and silica primary particles are formed. As the reaction further proceeds, the primary particles are connected in the form of a string of beads to generate a gel having a three-dimensional structure, for example.

The gelled compound obtained by the gelation is preferably subjected to aging treatment after the gelation reaction. The aging treatment causes further growth of the primary particle of a gel having a three-dimensional structure obtained by gelation, for example, and this allows the size of the particle itself to be increased. As a result, the contact state of the neck where particles are in contact with one another can be increased from a point contact to a surface contact. The gel which has been subjected to the aging treatment improves its strength, for example, and this improves the strength of the three-dimensional basic structure after pulverization. This prevents, in the drying step after coating of the pulverized product, the pore size of the void-provided structure obtained by deposition of the three-dimensional basic structures from shrinking in accordance with solvent volatilization during the drying process, for example.

The aging treatment can be performed, for example, by incubating the gelled compound at a predetermined temperature for a predetermined time. The predetermined temperature is not particularly limited, and the lower limit thereof is, for example, 30° C. or more, 35° C. or more, or 40° C. or more, the upper limit thereof is, for example, 80° C. or less, 75° C. or less, or 70° C. or less, and the predetermined temperature is, for example, in the range from 30° C. to 80° C., 35° C. to 75° C., or 40° C. to 70° C. The predetermined time is not particularly limited, and the lower limit is, for example, 5 hours or more, 10 hours or more, or 15 hours or more, the upper limit is, for example, 50 hours or less, 40 hours or less, or 30 hours or less, and the predetermined time is, for example, in the range from 5 hours to 50 hours, 10 hours to 40 hours, or 15 hours to 30 hours. An optimal condition for the aging is, for example, the condition mainly aiming for increase in the size of the silica primary particle and increase in the contact area of the neck. Furthermore, it is preferable to take the boiling point of a solvent to be used into consideration. For example, when the aging temperature is too high, there is a possibility that the solvent excessively volatilizes, which causes defectiveness such that the pore of the three-dimensional void-provided structure closes due to the condensation of the concentration of a coating liquid (gel liquid). On the other hand, for example, when the aging temperature is too low, there is a possibility not only that a sufficient effect of the aging is not brought about but also that temperature variations over time in a mass production process increase, which causes products with poor quality to be produced.

The same solvent as the solvent used in the gelation treatment can be used in the aging treatment, for example. Specifically, the aging treatment is preferably applied to a reactant (the solvent containing the gelled compound) after the gelation treatment. The mol number of residual silanol groups contained in the gel (the gelled compound, for example, the gelled silicon compound) after completion of the aging treatment after gelation is, for example, the proportion of the residual silanol group with the mol number of alkoxy groups of the added raw material (for example, the monomer compound precursor) being considered as 100, and the lower limit thereof is, for example, 50% or more, 40% or more, or 30% or more, the upper limit thereof is, for example, 1% or less, 3% or less, or 5% or less, and the mol number is, for example, in the range from 1% to 50%, 3% to 40%, or 5% to 30%. For the purpose of improving the hardness of a gel, for example, the lower the mol number of the residual silanol groups, the better. When the mol number of the silanol groups is too high, for example, there is a possibility that the void-provided structure cannot be held until crosslinking is done in the precursors of the silicone porous body. On the other hand, when the mol number of the silanol groups is too low, for example, there is a possibility that the pulverized products of the gelled compound cannot be crosslinked in a step of preparing the liquid containing microporous particles (for example, suspension) and/or subsequent steps, which hinders a sufficient film strength from being imparted. Note that while the aforementioned description is described with reference to a silanol group as an example, the same phenomenon shall be applied to various functional groups in the case where a monomer silicon compound is modified with various reactive functional groups, for example.

After gelation of the monomer compound in the gelation solvent, the obtained gelled compound is pulverized. The gelled compound in the gelation solvent which has not been processed may be pulverized or the gelation solvent may be substituted with another solvent and the gelled compound in the substituted solvent may be pulverized, for example. Furthermore, if the catalyst and solvent used in the gelation reaction remain after the aging step, which causes gelation of the liquid over time (pot life) and decreases the drying efficiency in the drying step, it is preferable to substitute the gelation solvent with another solvent. Hereinafter, such a solvent for substitution may be also referred to as a “pulverization solvent”.

The pulverization solvent is not limited to particular solvents, and can be, for example, an organic solvent. The organic solvent can be, for example, a solvent having a boiling point at 130° C. or less, 100° C. or less, or 85° C. or less. Specific examples of the organic solvent include isopropyl alcohol (IPA), ethanol, methanol, butanol, propylene glycol monomethyl ether (PGME), methyl cellosolve, acetone, and dimethylformamide (DMF). One of the pulverization solvents may be used alone or two or more of them may be used in combination.

The combination of the gelation solvent and the pulverization solvent is not limited to particular combinations, and the combination can be, for example, the combination of DMSO and IPA, the combination of DMSO and ethanol, the combination of DMSO and methanol, and the combination of DMSO and butanol. Substitution of the gelation solvent with the pulverization solvent makes it possible to form a coating film with uniform quality in the coating film formation described below, for example.

The method of pulverizing the gelled compound is not limited to particular methods. Examples of the apparatus for pulverizing include: pulverizing apparatuses utilizing a cavitation phenomenon such as an ultrasonic homogenizer and a high-speed rotating homogenizer; and pulverizing apparatuses of causing oblique collision of liquids at a high pressure. An apparatus such as a ball mill that performs media pulverization physically destroys the void-provided structure of a gel in pulverization, for example. On the other hand, a cavitation-type pulverizing apparatus such as a homogenizer, which is preferable in the present invention, peels the contact surface of silica particles, which are already contained in a gel three-dimensional structure and bonded relatively weakly, with a high speed shearing force owing to a media-less method, for example. Thus, a sol three-dimensional structure to be obtained can hold the void-provided structure having a particle size distribution of a certain range and can form the void-provided structure again by deposition in coating and drying, for example. The condition for the pulverization is not limited to particular conditions, and is preferably a condition that allows a gel to be pulverized without volatilizing a solvent by instantaneously imparting a high speed flow, for example. For example, it is preferable to pulverize the gelled silicon compound so as to obtain pulverized products having the above described particle size variations (for example, volume average particle size or particle size distribution). If the pulverization time, the pulverization strength, or the like is lacking, for example, there is a possibility not only that coarse particles remain, which hinders dense pores from being formed but also that defects in appearance increase, which hinders high quality from being achieved. On the other hand, if the pulverization time, the pulverization strength, or the like is too much, for example, there is a possibility that a finer sol particle than a desired particle size distribution is obtained and the size of a void space deposited after coating and drying is too fine to satisfy a desired porosity.

In the manner described above, a liquid (for example, suspension) containing the microporous particles (pulverized products of a gelled compound) can be prepared. By further adding a catalyst for chemically bonding the microporous particles after or during the preparation of the liquid containing the microporous particles, a liquid containing the microporous particles and the catalyst can be prepared. The amount of the catalyst to be added is not particularly limited, and the amount of the catalyst to be added relative to the weight of the microporous particle (pulverized product of the gelled compound) is, for example, in the range from 0.01 wt % to 20 wt %, 0.05 wt % to 10 wt %, or 0.1 wt % to 5 wt %. This catalyst may be a catalyst (crosslinking reaction accelerator) that promotes the crosslinking bond among the microporous particles or a strength improver that improves the strength of the void-provided layer, and the crosslinking accelerator may also serve as the strength improver, for example. As the chemical reaction of chemically bonding the microporous particles, it is preferable to utilize the dehydration condensation reaction of a residual silanol group contained in a silica sol molecule. By promoting the reaction between the hydroxyl groups of the silanol group by the catalyst, the continuous formation of a film in which the void-provided structure is cured in a short time can be performed. Examples of the catalyst include photoactive catalysts and thermoactive catalysts. The photoactive catalyst allows the chemical bond (for example, crosslinking bond) among the microporous particles without heating in the void-provided layer forming step, for example. This makes it possible to maintain a higher proportion of void space because the shrinkage of the whole void-provided layer in the void-provided layer forming step is less liable to occur, for example. In addition to or instead of the catalyst, a substance (catalyst generator) that generates a catalyst may be used. As described above, the catalyst may be a catalyst (crosslinking reaction accelerator) that promotes the crosslinking bond among the microporous particles or a strength improver that improves the strength of the void-provided layer, and the crosslinking accelerator may also serve as the strength improver, for example. In this case, the catalyst generator may be a substance that generates a catalyst which serves as the crosslinking reaction accelerator or the strength improver. For example, in addition to or instead of the photoactive catalyst, a substance (photocatalyst generator) that generates a catalyst by light irradiation may be used. For example, in addition to or instead of the thermoactive catalyst, a substance (thermal catalyst generator) that generates a catalyst by heating may be used. The photocatalyst generator is not limited to particular photocatalyst generators, and examples thereof include photobase generators (substances that generate basic catalysts by light irradiation) and photoacid generators (substances that generate acidic catalysts by light irradiation). Among them, the photobase generator is preferable. Examples of the photobase generator include 9-anthrylmethyl N, N-diethylcarbamate (product name: WPBG-018), (E)-1-[3-(2⁻hydroxyphenyl)-2-propenoyl]piperidine (product name: WPBG-027), 1-(anthraquinon-2-yDethyl imidazolecarboxylate (product name: WPBG-140), 2-nitrophenylmethyl 4-methacryloyloxypiperidine-1-carboxylate (product name: WPBG-165), 1,2-diisopropyl-3-[bis(dimethylamino) methylenelguanidium 2-(3-benzoylphenyl)propionate (product name: WPBG-266), 1,2-dicyclohexyl-4,4,5,5-tetramethylbiguanidium n-butyltriphenylborate (product name: WPBG-300), 2-(9-oxoxanthen-2-yl)propionic acid 1,5,7-triazabicyclo[4.4.0] dec-5-ene (Tokyo Kasei Kogyo Co., Ltd.), and a compound containing 4-piperidinemethanol (product of Heraeus, product name: HDPD-PB100). Note here that each product with the name including “WPBG” is a product of Wako Pure Chemical Industries, Ltd. Examples of the photoacid generator include aromatic sulfonium salt (product of ADEKA, product name: SP-170), triarylsulfonium salt (product of San-Apro Ltd., product name: CPI101A), and aromatic iodonium salt (product of Ciba Japan, product name: Irgacure 250). The catalyst for chemically bonding the microporous particles is not limited to the photoactive catalyst and the photocatalyst generator, and can be, for example, a thermoactive catalyst or a thermal catalyst generator such as urea. Examples of the catalyst for chemically bonding the microporous particles include base catalysts such as potassium hydroxide, sodium hydroxide, and ammonium hydroxide; and acid catalysts such as a hydrochloric acid, an acetic acid, and an oxalic acid. Among them, the base catalyst is preferable. The catalyst or the catalyst generator for chemically bonding the microporous particles can be used by adding it to a sol particle liquid (for example, suspension) containing the pulverized products (microporous particles) right before the coating, or the catalyst or the catalyst generator can be used as a mixture by mixing it with a solvent, for example. The mixture may be, for example, a coating liquid obtained by adding the catalyst or the catalyst generator directly to the sol particle liquid, a solution obtained by dissolving the catalyst or the catalyst generator in a solvent, or a dispersion liquid obtained by dispersing the catalyst or the catalyst generator into a solvent. The solvent is not limited to particular solvents, and examples thereof include various organic solvents, water, and buffer solutions.

For example, in the case where the microporous particle is a pulverized product of a gelled silicon compound obtained from a silicon compound containing at least three or less functional groups having saturated bonds, a crosslinking assisting agent for indirectly bonding the microporous particles may further be added after or during preparation of a liquid containing the microporous particles. This crosslinking assisting agent penetrates among particles and interacts with or bonds to the particles, which helps to bond particles relatively distanced from one another and makes it possible to increase the strength efficiently. As the crosslinking assisting agent, a multi-crosslinking silane monomer is preferable. Specifically, the multi-crosslinking silane monomer may have at least two and at most three alkoxysilyl groups, the chain length between the alkoxysilyl groups may be 1-10C, and the multi-crosslinking silane monomer may contain an element other than carbon, for example. Examples of the crosslinking assisting agent include bis(trimethoxysilyl)ethane, bis(triethoxysilyDethane, bis(trimethoxysilyl)methane, bis(triethoxysilyl)methane, bis(triethoxysilyl)propane, bis(trimethoxysilyl)propane, bis(triethoxysilyl)butane, bis(trimethoxysilyl)butane, bis(triethoxysilyl)pentane, bis(trimethoxysilyl)pentane, bis(triethoxysilyl)hexane, bis(trimethoxysilyl)hexane, bis(trimethoxysilyl)-N-butyl-N-propyl-ethane-1,2-diamine, tris-(3-trimethoxysilylpropyl)isocyanurate, and tris-(3-triethoxysilylpropyl)isocyanurate. The amount of the crosslinking assisting agent to be added is not particularly limited, and the amount of the crosslinking assisting agent to be added relative to the weight of the silicon compound microporous particle is, for example, in the range from 0.01 wt % to 20 wt %, 0.05 wt % to 15 wt %, or 0.1 wt % to 10 wt %.

Subsequently, a resin film (hereinafter, also referred to as a “base”) is coated with the liquid containing the microporous particles (for example, suspension) (coating step). The coating can be performed, for example, by the various coating methods described below but not limited thereto. By directly coating the resin film with the liquid containing the microporous particles (for example, pulverized products of a gelled silica compound), a coating film containing the microporous particles and the catalyst can be formed. The coating film can also be referred to as coating layer, for example. Formation of the coating film causes the settlement and deposition of the pulverized product whose three-dimensional structure has been destroyed, for example, and this allows a new three-dimensional structure to be formed. Note that the microporous particle-containing liquid may not contain a catalyst for chemically bonding the microporous particles, for example. For example, as described below, the precursor forming step may be performed after the catalyst has been sprayed to the coating film or while spraying the catalyst to the coating film. On the other hand, the microporous particle-containing liquid may contain a catalyst for chemically bonding the microporous particles, and the precursor of the porous body may be formed by chemically bonding the microporous particles by the catalysis of the catalyst contained in the coating film.

The solvent (hereinafter, also referred to as a “coating solvent”) is not limited to particular solvents, and can be, for example, an organic solvent. The organic solvent can be, for example, a solvent having a boiling point at 150° C. or less. Specific examples of the solvent include IPA, ethanol, methanol, n-butanol, 2-butanol, isobutyl alcohol, and pentanol, and the examples of the pulverization solvent described above can be used. In the case where the present invention includes a step of pulverizing the gelled compound, for example, the pulverization solvent containing the pulverized products of the gelled compound can be used without processing in the step of forming the coating film.

In the coating step, for example, it is preferable to coat the base with the sol pulverized products dispersed in the solvent (hereinafter, also referred to as a “sol particle liquid”). After coating the base with the sol particle liquid of the present invention and drying it, by chemically crosslinking the particles, the continuous formation of a void-provided layer having a film strength of a certain level or more can be performed. The “sol” in the present invention denotes a fluidic state in which silica sol particles each having a nano three-dimensional structure holding a part of the void-provided structure are dispersed in a solvent by pulverization of the three-dimensional structure of a gel.

The concentration of the pulverized product in the solvent is not particularly limited, and is, for example, in the range from 0.3% to 50%(v/v), 0.5% to 30%(v/v), or 1.0% to 10%(v/v). When the concentration of the pulverized product is too high, there is a possibility that the fluidity of the sol particle liquid decreases significantly, which causes aggregates and coating stripes in coating, for example. On the other hand, when the concentration of the pulverized product is too low, there is a possibility not only that the drying of the sol particle solvent takes a relatively long time but also that the residual solvent right after the drying increases, which may decrease the porosity, for example.

There is no particular limitation on the physical property of the sol. The shear viscosity of the sol is, for example, 100 cPa·s or less, 10 cPa·s or less, or 1 cPa·s or less, for example, at the shear rate of 10001/s. When the shear viscosity is too high, for example, there is a possibility that the coating stripes are generated, which causes defectiveness such as decrease in the transfer rate in the gravure coating. In contrast, when the shear viscosity is too low, for example, there is a possibility that the thickness of the wet coating (coating) during coating cannot be increased and a desired thickness cannot be obtained after drying.

The coating amount of the pulverized product relative to the base is not particularly limited, and can be determined appropriately, for example, according to the thickness of a desired silicone porous body. As a specific example, in the case of forming the silicone porous body having a thickness of 0.1 μm to 1000 μm, the coating amount of the pulverized product relative to the base is, for example, in the range from 0.01 μg to 60000 μg, 0.1 μg to 5000 μg, or 1 μg to 50 μg per square meter of the base. Although it is difficult to uniquely define a preferable coating amount of the sol particle liquid because it depends on the concentration of a liquid, the coating method, or the like, for example, it is preferable that a coating layer is as thin as possible in consideration of productivity. When the coating amount (application amount) is too much, for example, there is a high possibility that a solvent is dried in a drying oven before volatilizing. When the solvent is dried before forming the void-provided structure by the settlement and deposition of the nano pulverized sol particles in the solvent, there is a possibility that formation of void spaces is inhibited and the proportion of void space decreases. On the other hand, when the coating amount is too little, there is a possibility of increasing the risk of causing coating cissing due to unevenness of a base, variations in hydrophilicity and hydrophobicity, and the like.

Furthermore, for example, the production method of the present invention includes a step of drying a coating film formed by applying the liquid containing the microporous particles as described above. The drying treatment in the drying step is aimed not only for removing the solvent (solvent contained in the sol particle liquid) from the precursor of the coating film but also for causing the settlement and deposition of the sol particles to form a void-provided structure in the drying treatment, for example. The temperature for the drying treatment is, for example, in the range from 50° C. to 250° C., 60° C. to 150° C., or 70° C. to 130° C., and the time for the drying treatment is, for example, in the range from 0.1 minutes to 30 minutes, 0.2 minutes to 10 minutes, or 0.3 minutes to 3 minutes. Regarding the temperature and time for the drying treatment in relation to continuous productivity and high porosity expression, the lower the better and the shorter the better, for example. When the condition is too strict, there is a possibility of causing the following problems, for example. That is, when the base is a resin film, for example, the base extends in a drying oven as the temperature approaches the glass-transition temperature of the base, which causes defects such as cracks in a formed void-provided structure right after coating. On the other hand, when the condition is too mild, there is a possibility of causing the following problems, for example. That is, since the film contains a residual solvent when it comes out of the drying oven, defects in appearance such as scratches are caused when the film rubs against a roller in the next step.

The drying treatment may be, for example, natural drying, drying by heating, or drying under reduced pressure. The drying method is not limited to particular methods, and a common heating unit can be used, for example. Examples of the heating unit include a hot air fan, a heating roll, and a far-infrared heater. Among them, in view of performing continuous production industrially, drying by heating is preferable. The solvent to be used is preferably a solvent having a low surface tension in view of reducing the shrinkage stress in accordance with the solvent volatilization in drying and reducing the crack phenomenon of the void-provided layer (the silicone porous body) due to the shrinkage stress. The solvent can be, for example, lower alcohol typified by isopropyl alcohol (IPA), hexane, perfluorohexane, and the like. The solvent, however, is not limited thereto. The surface tension may be reduced by adding a small amount of a perfluoro surfactant or a small amount of a silicon surfactant to the IPA and the like.

Furthermore, the production method of the laminated film of the present invention forms the porous body (void-provided layer) by chemically bonding the microporous particles by the catalysis, for example (void-provided layer forming step). Thereby, the three-dimensional structure of the pulverized product in the precursor of the coating film is immobilized, for example. The catalyst may be a crosslinking accelerator that promotes the crosslinking reaction among the microporous particles, for example. In the case of immobilizing the three-dimensional structure by conventional sintering, for example, the dehydration condensation of a silanol group and the formation of a siloxane bond are induced by high temperature treatment at 200° C. or more. In the present invention, for example, the void-provided structure can be formed and immobilized continuously at about 100° C. which is relatively low for less than several minutes which is short without damaging the base (resin film) by causing various additives, which catalyze the dehydration condensation reaction, to react.

The method of chemically bonding the particles is not limited to particular methods, and can be determined appropriately according to the type of the gelled silicon compound, for example. Specifically, for example, the chemical bond can be a chemical crosslinking bond among the pulverized products. Besides this, for example, when inorganic particles such as titanium oxide particles are added to the pulverized products, the inorganic particles and the pulverized products can be chemically bonded by crosslinking. Furthermore, there are a case of using a biocatalyst such as an enzyme and a case of chemically crosslinking the pulverized product and a catalyst at a site which is different from a catalytic activity site. Thus, the present invention can be applied not only to a void-provided layer (silicone porous body) formed of the sol particles but also to an organic-inorganic hybrid void-provided layer, a host-guest void-provided layer, and the like, for example. The present invention, however, is not limited thereto.

It is not particularly limited at which stage the chemical reaction (void-provided layer forming step) in the presence of the catalyst (crosslinking reaction accelerator) is performed (caused) in the production method of the present invention. For example, in the production method of a laminated film of the present invention, the drying step may also serve as the void-provided layer forming step. Furthermore, for example, the void-provided layer forming step of chemically bonding the microporous particles by the catalysis may be performed after the drying step. For example, as described above, the catalyst (crosslinking reaction accelerator) may be a photoactive catalyst, and the porous body (void-provided layer) may be formed by chemically bonding the microporous particle by light irradiation in the void-provided layer forming step. Furthermore, the catalyst may be a thermoactive catalyst, and the porous body (void-provided layer) may be formed by chemically bonding the microporous particles by heating in the void-provided layer forming step.

The chemical reaction can be performed, for example, by heating the coating film containing the catalyst or the catalyst generator preliminarily added to the sol particle liquid (for example, suspension) or irradiating the coating film containing the catalyst or the catalyst generator preliminarily added to the sol particle liquid with light, by heating the coating film or irradiating the coating film with light after the catalyst or the catalyst generator has been sprayed to the coating film, or by heating the coating film or irradiating the coating film with light while spraying the catalyst or the catalyst generator to the coating film. The catalyst may be a crosslinking reaction accelerator that promotes the crosslinking reaction among the sol particles or a strength improver that improves the strength of the void-provided layer, and the crosslinking accelerator may also serve as the strength improver, for example. The accumulated light amount in the light irradiation is not particularly limited, and is, for example, in the range from 200 to 800 mJ/cm², 250 to 600 mJ/cm², or 300 to 400 mJ/cm² in terms of the wavelength at 360 nm. From the view point of preventing the effect from being insufficient due to the delay of decomposition of the catalyst generator by light absorption because of insufficient irradiation amount, the accumulated light amount is preferably 200 mJ/cm² or more. From the view point of preventing heat wrinkles from generating due to the damage on a base below a void-provided layer, the accumulated light amount is preferably 800 mJ/cm² or less. The conditions for the heat treatment are not limited to particular conditions. The heating temperature is, for example, 50° C. to 250° C., 60° C. to 150° C., or 70° C. to 130° C., the heating time is, for example, 0.1 to 30 minutes, 0.2 to 10 minutes, or 0.3 to 3 minutes. The step of drying the sol particle liquid (for example, suspension) may also serve as a step of performing a chemical reaction in the presence of the catalyst as described above. That is, in the step of drying the sol particle liquid (for example, suspension), the pulverized products (microporous particles) may be chemically bonded in the presence of the catalyst. In this case, by further heating the coating film after the drying step, the pulverized products (microporous particles) may be bonded more firmly. It is presumed that the chemical reaction in the presence of the catalyst may be caused also in the step of preparing the liquid (for example, suspension) containing the microporous particles and the step of coating the resin film with the liquid containing microporous particles. This presumption, however, does not limit the present invention by any means. The solvent to be used is preferably a solvent having a low surface tension in view of reducing the shrinkage stress in accordance with the solvent volatilization in drying and reducing the crack phenomenon of the void-provided layer due to the shrinkage stress, for example. The solvent can be, for example, lower alcohol typified by isopropyl alcohol (IPA), hexane, perfluorohexane, or the like. The solvent, however, is not limited thereto.

Subsequently, the pressure-sensitive adhesive/adhesive layer is formed on the void-provided layer (pressure-sensitive adhesive/adhesive layer forming step). This step is not particularly limited. For example, the pressure-sensitive adhesive/adhesive layer may be formed by applying a pressure-sensitive adhesive or an adhesive to the void-provided layer. The pressure-sensitive adhesive/adhesive layer may be formed on the void-provided layer using an adhesive tape in which the pressure-sensitive adhesive/adhesive layer is formed on a base by adhering the pressure-sensitive adhesive/adhesive layer side of the adhesive tape on the void-provided layer. In this case, the base of the adhesive tape may be kept adhered or peeled from the pressure-sensitive adhesive/adhesive layer. Note that the laminated film of the present invention may include an arbitrary component other than the resin film, the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer. The arbitrary component may be, for example, a layer other than the resin film, the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer, and may be, for example, a base of the adhesive tape.

Furthermore, the intermediate layer is formed by causing the void-provided layer to react with the pressure-sensitive adhesive/adhesive layer (intermediate layer forming step). This step is not particularly limited. For example, as described above, the intermediate layer may be formed by causing the void-provided layer and the pressure-sensitive adhesive/adhesive layer to react with each other by heating. The temperature of the reaction is, for example, 40° C. to 80° C., 50° C. to 70° C., or 55° C. to 65° C. The time for the reaction is, for example, 5 to 30 hours, 7 to 25 hours, or 10 to 20 hours.

Owing to the formation of the intermediate layer, the laminated film of the present invention in which the void-provided layer and the pressure-sensitive adhesive/adhesive layer are not easily peeled from each other can be formed, for example. While the reason (mechanism) for this is unknown, as described above, it is presumed that the void-provided layer and the pressure-sensitive adhesive/adhesive layer are not easily peeled from each other owing to the anchoring property (anchor effect) of the intermediate layer, for example. This reason (mechanism), however, is an example of a presumable reason (mechanism), and does not limit the present invention.

While the mechanism for forming the intermediate layer is unknown, for example, it is presumed that the intermediate layer is formed by the reaction between the void-provided layer and the pressure-sensitive adhesive/adhesive layer by the catalysis of the catalyst present in the void-provided layer. The catalyst present in the void-provided layer is not particularly limited, and may be, for example, a basic catalyst or an acidic catalyst. The basic catalyst (base catalyst) is not particularly limited, and the photobase generator may be, for example, a basic catalyst generated by light irradiation. The acid catalyst is not particularly limited, and the photoacid generator may be, for example, an acidic catalyst generated by light irradiation. The reaction between the void-provided layer and the pressure-sensitive adhesive/adhesive layer may be, as described above, the reaction (for example, crosslinking reaction) that generates a new chemical bond, for example.

For example, as described above, the intermediate layer forming step may also serve as a crosslinking reaction step of causing a crosslinking reaction in the void-provided layer. This provides a laminated film achieving an improved strength of the void-provided layer, superior film strength, and a property that a void-provided layer and a pressure-sensitive adhesive/adhesive layer are not easily peeled from each other. The crosslinking reaction caused in the void-provided layer in this state, as described above, proceeds by the catalysis of the catalyst (crosslinking reaction accelerator or strength improver) contained in the void-provided layer, for example. This description, however, does not limit the present invention.

The laminated film of the present invention can be produced in the manner as described above. Owing to its superior strength, for example, the laminated film produced by the production method of the present invention can be a porous body in the form of a roll, which brings about advantageous effects such as a superior manufacturing efficiency, a superior handleability, and the like.

The thus obtained laminated film (void-provided layer) of the present invention may further be stacked on another film (layer) to form a laminate having the porous structure, for example. In this case, the components of the laminate may be stacked through a pressure-sensitive adhesive or an adhesive, for example.

The components may be laminated by continuous treatment (so called Roll to Roll) using a long film, for example, in terms of efficiency. When the base is a molded product, an element, or the like, the base that has been subjected to a batch process may be laminated.

The method of forming a void-provided layer of the present invention on a base (resin film) is described below with reference to a continuous treatment process using FIGS. 1 to 3 as an example. FIG. 2 shows a step of adhering a protective film to a formed silicone porous body and winding the laminate. In the case of forming the silicone porous body on another functional film, the aforementioned method may be adopted or the formed silicone porous body may be adhered to another functional film that has been coated and dried, right before winding. The method of forming a film shown in FIG. 2 is an example, and the present invention is not limited thereto.

The base may be the resin film described in the description as to the laminated film of the present invention. In this case, the void-provided layer of the present invention can be obtained by forming the void-provided layer on the base. The void-provided layer of the present invention can be obtained also by forming the void-provided layer on the base and then stacking the void-provided layer with the base on the resin film described in the description as to the void-provided layer of the present invention.

FIG. 1 is a cross sectional view schematically showing an example of the process of forming the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer on the base (resin film) in this order in the present invention. In FIG. 1, the method of forming the void-provided layer includes: (1) a coating step of coating a base (resin film) 10 with a sol particle liquid 20″ containing pulverized products of a gelled compound; (2) a drying step of drying the sol particle liquid 20″ to form a dried coating film 20′; (3) a chemical treatment step (for example, crosslinking step) of applying chemical treatment (for example, crosslinking treatment) to the coating film 20′ to form a void-provided layer 20; (4) a pressure-sensitive adhesive/adhesive layer applying step (pressure-sensitive adhesive/adhesive layer forming step) of applying a pressure-sensitive adhesive/adhesive layer 30 to the void-provided layer 20; and (5) an intermediate layer forming step of causing the void-provided layer 20 to react with the pressure-sensitive adhesive/adhesive layer 30 to form an intermediate layer 22. The (3) chemical treatment step (crosslinking step) corresponds to the “void-provided layer forming step” in the production method of a laminated film of the present invention. In FIG. 1, the (5) intermediate layer forming step (hereinafter, also referred to as an “aging step”) also serves as a step of improving the strength of the void-provided layer 20 (crosslinking reaction step of causing a crosslinking reaction in the void-provided layer 20) so that the void-provided layer 20 changes to a void-provided layer 21 having a higher strength after the (5) intermediate layer forming step. The present invention, however, is not limited thereto, and the void-provided layer 20 may not change after the (5) intermediate layer forming step, for example. The pressure-sensitive adhesive/adhesive layer forming step is not limited to the application of the pressure-sensitive adhesive/adhesive layer, and an adhesive tape including a pressure-sensitive adhesive/adhesive layer may be adhered as described above. By the steps (1) to (5), as shown in FIG. 1, a laminated film in which the void-provided layer 21, the intermediate layer 22, and the pressure-sensitive adhesive/adhesive layer 30 are stacked on the resin film 10 in this order. The production method of a laminated film of the present invention may include steps other than the steps (1) to (5) appropriately.

In the (1) coating step, the method of coating the base with the sol particle liquid 20″ is not limited to particular methods, and a common method can be adopted. Examples of the method include a slot die method, a reverse gravure coating method, a micro-gravure method (micro-gravure coating method), a dip method (dip coating method), a spin coating method, a brush coating method, a roller coating method, a flexography method, a wire-bar coating method, a spray coating method, an extrusion coating method, a curtain coating method, and a reverse coating method. Among them, from the viewpoint of productivity, smoothness of a coating film, and the like, an extrusion coating method, a curtain coating method, a roller coating method, a micro-gravure coating method, and the like are preferable. The coating amount of the sol particle liquid 20″ is not particularly limited, and can be determined appropriately so as to obtain a void-provided layer 20 having an appropriate thickness, for example. The thickness of the void-provided layer 21 is not particularly limited, and is, for example, as described above.

In the (2) drying step, the sol particle liquid 20″ is dried (i.e., dispersion medium contained in sol particle liquid 20″ is removed) to form a coating film after drying (a precursor of the void-provided layer) 20′. There is no particular limitation on the condition for the drying treatment, and is as described above.

In the (3) chemical treatment step, the coating film 20′ containing the catalyst or the catalyst generator (for example, photoactive catalyst, photocatalyst generator, thermoactive catalyst, or thermal catalyst generator) which has been added before coating is irradiated with light or heated to chemically bond (for example, crosslink) the pulverized products in the coating film 20′, thereby forming a void-provided layer 20. The conditions for the light irradiation and heating in the (3) chemical treatment step are not limited to particular conditions, and are as described above.

There are no particular limitations on the conditions for the (4) pressure-sensitive adhesive/adhesive layer applying step (pressure-sensitive adhesive/adhesive layer forming step) and the (5) intermediate layer forming step, and are as described above, for example.

FIG. 2 schematically shows an example of a slot die coating apparatus and an example of the method of forming a void-provided layer using the same. Although FIG. 2 is a cross sectional view, hatching is omitted for viewability.

As shown in FIG. 2, the steps of the method using this apparatus are carried out while carrying a base 10 in one direction by rollers. The carrying speed is not particularly limited, and is, for example, in the range from 1 to 100 m/min, 3 to 50 m/min, or 5 to 30 m/min.

First, the base 10 is delivered from a delivery roller 101 and carried to a coating roller 102, and the (1) coating step of coating the base 10 with a sol particle liquid 20″ is carried out using the coating roller 102. Subsequently, the (2) drying step is carried out in an oven zone 110. In the coating apparatus shown in FIG. 2, a predrying step is carried out after the (1) coating step and before the (2) drying step. The predrying step can be carried out at room temperature without heating. In the (2) drying step, a heating unit 111 is used. As the heating unit 111, as described above, a hot air fan, a heating roll, a far-infrared heater, or the like can be used appropriately. For example, the (2) drying step may be divided into multiple steps, and the drying temperature may be set higher as coming to later steps.

The (3) chemical treatment step is carried out in a chemical treatment zone 120 after the (2) drying step. In the (3) chemical treatment step, for example, when the coating film 20′ after drying contains a photoactive catalyst, light is emitted from lamps (light irradiation units) 121 disposed above and below the base 10. On the other hand, for example, when the coating film 20′ after drying contains a thermoactive catalyst, the base 10 is heated using hot air fans 121 disposed above and below the base 10 instead of using the lamps (light irradiation devices) 121. By this crosslinking treatment, the pulverized products in the coating film 20′ are chemically bonded, and the void-provided layer 20 is cured and strengthened. Note that, although the (3) chemical treatment step is performed after the (2) drying step in the present example, as described above, there is no particular limitation at which stage in the production method of the present invention the chemical bond among the pulverized products is caused. For example, as described above, the (2) drying step may also serve as the (3) chemical treatment step. Even when the chemical bond is caused in the (2) drying step, the (3) chemical treatment step may be performed to make the chemical bond among the pulverized products firmer.

Furthermore, in the steps (for example, predrying step, the (1) coating step, step of preparing a coating liquid (for example, suspension), and the like) before the (2) drying step, the chemical bond among the pulverized products may be caused.

After the (3) chemical treatment step, the (4) pressure-sensitive adhesive/adhesive layer applying step (pressure-sensitive adhesive/adhesive layer forming step) of applying a pressure-sensitive adhesive or an adhesive to the void-provided layer 20 to form a pressure-sensitive adhesive/adhesive layer 30 in the pressure-sensitive adhesive/adhesive layer applying zone 130 a is performed using pressure-sensitive adhesive/adhesive layer applying units 131 a. Instead of applying the pressure-sensitive adhesive or the adhesive, for example, an adhesive tape including the pressure-sensitive adhesive/adhesive layer 30 may be adhered (taped) as described above.

Thereafter, the (5) intermediate layer forming step (aging step) is carried out in the intermediate layer forming zone (aging zone) 130 to cause the void-provided layer 20 to react with the pressure-sensitive adhesive/adhesive layer 30, thereby forming an intermediate layer 22. In this step, a crosslinking reaction is caused in the void-provided layer 20 so that it changes to a void-provided layer 21 having a higher strength as described above. The (5) intermediate layer forming step (aging step) may be performed by heating the void-provided layer 20 and the pressure-sensitive adhesive/adhesive layer 30 using hot air fans (heating units) 131 disposed above and below the base 10, for example. The heating temperature, the time, and the like are not particularly limited, and can be, for example, as described above.

After the (5) intermediate layer forming step (aging step), a laminate in which the void-provided layer 21 is formed on the base 10 is wound by a winding roller 105. In FIG. 2, the void-provided layer 21, which is a laminate, is protected by coating with a protecting sheet delivered from a roller 106. Instead of the protecting sheet, another layer formed of a long film may be stacked on the void-provided layer 21.

FIG. 3 schematically shows an example of a micro-gravure coating apparatus and an example of the method of forming a void-provided layer using the same. Although FIG. 3 is a cross sectional view, hatching is omitted for viewability.

As shown in FIG. 3, the steps of the method using this apparatus are carried out while carrying the base 10 in one direction by rollers as in FIG. 2. The carrying speed is not particularly limited, and is, for example, in the range from 1 to 100 m/min, 3 to 50 m/min, or 5 to 30 m/min.

First, the (1) coating step of coating the base 10 with a sol particle liquid 20″ is carried out while carrying the base 10 delivered from a delivery roller 201. As shown in FIG. 3, the coating with the sol particle liquid 20″ is performed using a liquid reservoir 202, a doctor (doctor knife) 203, and a micro-gravure 204. Specifically, the sol particle liquid 20′ in the liquid reservoir 202 is applied to the surface of the micro-gravure 204 and the coating of the surface of the base 10 is performed using the micro-gravure 204 while controlling the thickness to a predetermined thickness using a doctor 203. The micro-gravure 204 is merely an illustrative example. The present invention is not limited thereto, and any other coating unit may be adopted.

Subsequently, the (2) drying step is performed. Specifically, as shown in FIG. 3, the base 10 coated with the sol particle liquid 20″ is carried into an oven zone 210 and the sol particle liquid 20″ is dried by heating using heating units 211 disposed in the oven zone 210. The heating units 211 can be, for example, the same as those shown in FIG. 2. For example, the (2) drying step may be divided into multiple steps by dividing the oven zone 210 into multiple sections, and the drying temperature may be set higher as coming to later steps. The (3) chemical treatment step is carried out in a chemical treatment zone 220 after the (2) drying step. In the (3) chemical treatment step, for example, when the coating film 20′ after drying contains a photoactive catalyst, light is emitted from lamps (light irradiation units) 221 disposed above and below the base 10. On the other hand, for example, when the coating film 20′ after drying contains a thermoactive catalyst, the base 10 is heated using hot air fans (heating units) 221 disposed above and below the base 10 instead of using lamps (light irradiation devices) 221. By this crosslinking treatment, the pulverized products in the coating film 20′ are chemically bonded, and the void-provided layer 20 is formed.

After the (3) chemical treatment step, the (4) pressure-sensitive adhesive/adhesive layer applying step (pressure-sensitive adhesive/adhesive layer forming step) of applying a pressure-sensitive adhesive or an adhesive to the void-provided layer 20 to form a pressure-sensitive adhesive/adhesive layer 30 is performed in the pressure-sensitive adhesive/adhesive layer applying zone 230 a using pressure-sensitive adhesive/adhesive layer applying units 231 a. Instead of applying the pressure-sensitive adhesive or the adhesive, for example, an adhesive tape including the pressure-sensitive adhesive/adhesive layer 30 may be adhered (taped) as described above.

Thereafter, the (5) intermediate layer forming step (aging step) is carried out in the intermediate layer forming zone (aging zone) 230 to cause the void-provided layer 20 to react with the pressure-sensitive adhesive/adhesive layer 30, thereby forming an intermediate layer 22. In this step, the void-provided layer 20 changes to a void-provided layer 21 having a higher strength as described above. The (5) intermediate layer forming step (aging step) may be performed by heating the void-provided layer 20 and the pressure-sensitive adhesive/adhesive layer 30 using hot air fans (heating units) 231 disposed above and below the base 10, for example. The heating temperature, the time, and the like are not particularly limited, and can be, for example, as described above.

After the (5) intermediate layer forming step (aging step), a laminate in which the void-provided layer 21 is formed on the base 10 is wound by a winding roller 251. Thereafter, for example, another layer may be stacked on the laminated film. Furthermore, another layer may be stacked on the laminated film before winding the laminate by the winding roller 251, for example.

[3. Optical Element]

The optical element of the present invention is characterized in that it includes the optical laminate of the present invention as described above. The optical element of the present invention is characterized in that it includes the optical laminate of the present invention, and other configurations are by no means limited. The optical element of the present invention may further include another layer besides the optical laminate of the present invention, for example.

Furthermore, the optical element of the present invention includes the optical laminate of the present invention as a low reflective layer, for example. The optical element of the present invention may further include another layer besides the optical laminate of the present invention, for example. The optical element of the present invention is, for example, in the form of a roll.

EXAMPLES

The examples of the present invention are described below. The present invention, however, is not limited by the following examples.

Example 1

In the present example, a laminated film of the present invention (laminated film roll) was produced as described below.

(1) Gelation of Silicon Compound

0.95 g of MTMS which is the precursor of a silicon compound was dissolved in 2.2 g of DMSO. 0.5 g of 0.01 mol/L oxalic acid aqueous solution was added to the mixture, and the resultant was stirred at room temperature for 30 minutes to hydrolyze MTMS, thereby preparing tris(hydroxy) methylsilane.

0.38 g of ammonia water having a concentration of 28% and 0.2 g of pure water were added to 5.5 g of DMSO, then the aforementioned mixture that had been subjected to the hydrolysis treatment was added thereto, and the resultant was stirred at room temperature for 15 minutes to gelate tris(hydroxy)methylsilane, thereby obtaining a gelled silicon compound.

(2) Aging Treatment

The aging treatment was carried out as follows. The mixture that had been subjected to the gelation treatment was incubated at 40° C. for 20 hours.

(3) Pulverizing Treatment and Addition of Photobase Generator

Subsequently, the gelled silicon compound that had been subjected to the aging treatment was granulated into pieces of several millimeters to several centimeters using a spatula. 40 g of IPA was added thereto, the mixture was stirred lightly and then was allowed to stand still at room temperature for 6 hours, and a solvent and a catalyst in the gel were decanted. This decantation treatment was repeated three times, and the solvent replacement was completed. Then, the gelled silicon compound in the mixture was subjected to high pressure media-less pulverization. This pulverizing treatment was carried out using a homogenizer (product of SMT Corporation, product name: UH-50) as follows. That is, 1.18 g of gel and 1.14 g of IPA were added to 5 cc screw bottle and pulverized for 2 minutes at 50 W and 20 kHz.

The gelled silicon compound in the mixture was pulverized by the pulverizing treatment, whereby the mixture was changed to a sol particle liquid of the pulverized product. The volume average particle size showing particle size variations of the pulverized products contained in the mixture measured by a dynamic light scattering nanotrac particle size analyzer (product of NIKKISO CO., LTD., product name: UPA-EX150) was 0.50 to 0.70. 0.031 g of IPA (isopropyl alcohol) solution of 1.5 wt % photobase generator (Wako Pure Chemical Industries, Ltd., product name: WPBG266, a substance (a crosslinking reaction accelerator as well as a strength improver that improves the strength of a void-provided layer) that generates a catalyst by light irradiation) was added to 0.75 g of the sol particle liquid, thereby preparing a coating liquid. Note that the steps (1) to (3) corresponds to the “microporous particle-containing liquid preparation step” of preparing the microporous particle-containing liquid in the production method of the laminated film of the present invention.

(4) Formation of Coating Film and Silicone Porous Body (Void-Provided Layer)

The surface of a base (a resin film, length: 100 m) made of polyethylene terephthalate (PET) was coated with the coating liquid by bar coating, thereby forming a coating film (coating step). 6 μL of the sol particle liquid was applied to per square millimeter of the surface of the base. The coating film was dried at 100° C. for 1 minute to from a silicone porous body film having a thickness of 1 μm (drying step). The porous body film after drying was irradiated with UV light to form a void-provided layer (void-provided layer forming step). The accumulated light amount in the UV irradiation was 350 mJ/cm² in terms of the wavelength at 360 nm.

(5) Formation of Pressure-Sensitive Adhesive/Adhesive Layer and Intermediate Layer

Furthermore, a pressure-sensitive adhesive/adhesive layer (acrylic pressure-sensitive adhesive) was applied to the void-provided layer so as to have a thickness of about 20 μm. Thereafter, the void-provided layer together with the pressure-sensitive adhesive/adhesive layer (pressure-sensitive adhesive) was subjected to thermal aging at 60° C. for 22 hours so as to cause the pressure-sensitive adhesive (pressure-sensitive adhesive/adhesive layer) to react with the void-provided layer, thereby forming an intermediate layer (intermediate layer forming step). The resultant was wound to obtain a roll. In the manner as described above, a laminated film roll in which a low refractive index film (void-provided layer), an intermediate layer, and a pressure-sensitive adhesive/adhesive layer are stacked on a resin film in this order was produced.

Example 2

A laminated film roll was produced in the same manner as in Example 1 except that 0.018 g of 5 wt % 1,2-bis(trimethoxysilyl) ethane was added to 0.75 g of the sol liquid after addition of the photobase generator solution to adjust the coating liquid in the “(3) Pulverizing treatment and addition of photobase generator” step of Example 1.

Example 3

A laminated film roll was produced in the same manner as in Example 1 except that the amount of the photobase generator added to 0.75 g of the sol liquid was 0.054 g in the “(3) Pulverizing treatment and addition of photobase generator” step of Example 1.

Example 4

A laminated film roll was produced in the same manner as in Example 3 except that tris(trimethoxysilylpropyl) isocyanurate was used instead of 1,2-bis(trimethoxysilyl) ethane used in Example 3.

Example 5

A laminated film roll was produced in the same manner as in Example 2 except that a pulverized alumina sol liquid was used instead of the sol particle liquid. In the present example, 13 parts by weight of water was added to 20 parts by weight of alumina sol liquid produced by Kawaken Fine Chemicals Co., Ltd., the resultant was heated at 80° C., 3 parts by weight of NH₃ was added thereto, the resultant was heated at 80° C. for 10 hours for gelation, and the resultant was pulverized, thereby preparing the pulverized alumina sol liquid. In the present example, the refractive index of the void-provided layer (low refractive index film) obtained from the pulverized alumina sol liquid was 1.24.

Example 6

A laminated film roll was produced in the same manner as in Example 2 except that a pulverized cellulose nanofiber sol liquid was used instead of the sol particle liquid. In the present example, n-hexadecyltrimethylammonium chloride and urea were dissolved in the cellulose nanofiber sol liquid produced by SUGINO MACHINE LIMITED, MTMS was added thereto for hydrolysis, the resultant was heated at 60° C. for 20 hours for gelation, and the resultant was pulverized, thereby preparing the pulverized cellulose nanofiber sol liquid. In the present example, the refractive index of the void-provided layer (low refractive index film) obtained from the pulverized cellulose nanofiber sol liquid was 1.19.

Example 7

A laminated film roll was produced in the same manner as in Example 2 except that a dispersion liquid of hollow nanoparticles (product name: THRULYA4320, product of NISSAN CHEMICAL INDUSTRIES, LTD.) was used instead of the sol particle liquid. In the present example, the refractive index of the void-provided layer (low refractive index film) obtained from the dispersion liquid of the hollow nanoparticles was 1.19.

Example 8

A laminated film roll was produced in the same manner as in Example 2 except that a dispersion liquid of nanoclay (product of NISSAN CHEMICAL INDUSTRIES, LTD.) was used instead of the sol particle liquid. In the present example, the refractive index of the void-provided layer (low refractive index film) obtained from the dispersion liquid of the nanoclay was 1.24.

Example 9

A laminated film roll was produced in the same manner as in Example 2 except that a dispersion liquid of nanoballoon (product name, product of GRANDEX Co., Ltd.) was used instead of the sol particle liquid. In the present example, the refractive index of the void-provided layer (low refractive index film) obtained from the dispersion liquid of the nanoballoon was 1.15.

Example 10

A laminated film roll was produced in the same manner as in Example 2 except that a dispersion liquid (concentration: 15 wt %) of needle silica gel IPA-ST-UP (product name, product of NISSAN CHEMICAL INDUSTRIES, LTD.) was used instead of the sol particle liquid and IPA was added to the resultant so as to dilute it to the concentration of 5 wt %. In the present example, the refractive index of the void-provided layer (low refractive index film) obtained from the dispersion liquid was 1.19.

Comparative Example 1

A laminated film was produced in the same manner as in Example 1 except that aging at 60° C. for 22 hours was performed before the application of a pressure-sensitive adhesive/adhesive layer (pressure-sensitive adhesive) to a void-provided layer and the aging was not performed after the application of the pressure-sensitive adhesive/adhesive layer (pressure-sensitive adhesive) in the “(5) Formation of pressure-sensitive adhesive/adhesive layer and intermediate layer” step of Example 1.

Comparative Example 2

A laminated film roll was produced in the same manner as in Example 1 except that a sliced piece of a PET base was used instead of a long PET base, a photobase generator was not added in the “(3) Pulverizing treatment and addition of photobase generator” of Example 1, and a thermal aging step was omitted in the “(5) Formation of pressure-sensitive adhesive/adhesive layer and intermediate layer” step of Example 1. A sliced piece of a PET base was used instead of a long PET base because the void-provided layer was inferior in strength and flexibility and it was difficult to produce the laminated film continuously in the shape of a roll.

The results of the examples and comparative examples are shown in Table 1. The refractive index, peel strength, and haze were measured by the aforementioned method. The formation of the intermediate layer was checked with a cross sectional photograph by a scanning electron microscope (SEM). FIG. 4A shows a cross sectional photograph (cross sectional SEM image) of the laminated film roll of Example 1 and FIG. 4B shows a cross sectional photograph (cross sectional SEM image) of the laminated film roll of Example 7. As can be seen from FIGS. 4A and 4B, a part of the void-provided layer and a part of the pressure-sensitive adhesive/adhesive layer (pressure-sensitive adhesive) are united to form an intermediate layer. It was also confirmed that the intermediate layer was formed in Examples 2 to 6 and 8 to 10 and the intermediate layer was not formed in Comparative Examples 1 to 2. As to the storage stability, the coating liquid was left for one week at room temperature and the change in the coating liquid was visually observed.

TABLE 1 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 7 Ex. 10 Comp. Ex. 1 Comp. Ex. 2 Refractive 1.14 1.15 1.16 1.15 1.19 1.19 1.15 1.11 index Peel 2N/25 mm 3N/25 mm 2N/25 mm 2N/25 mm 1.5N/25 mm 5N/25 mm 1.0N/25 mm 0.1N/25 mm strength Storage Good Good Good Good Good Good Good Good stability No change No change No change No change No change No change No change in No change in in 1 week in 1 week in 1 week in 1 week in 1 week in 1 week 1 week 1 week Haze 0.4  0.4  0.4  0.4  0.5  0.3  0.4  0.3  Intermediate Formed Formed Formed Formed Formed Formed Not formed Not formed layer

As shown in Table 1, Examples 1 to 4, in each of which the intermediate layer forming step (aging step) was performed, each showed a peel strength higher than that of Comparative Example 1, in which the intermediate layer forming step (aging step) was not performed and the intermediate layer was not formed. Examples 1 to 4 each maintained a very low refractive index from 1.14 to 1.16, which is not greatly different from that of Comparative Example 1. As described above, a void-provided layer (low refractive index film) having a low refractive index was obtained in each of Examples other than Examples 1 to 4. This shows that the laminated films of Examples achieved both a high proportion of void space and a high film strength. Furthermore, since the laminated films of Examples 1 to 4 each maintained a very low haze value of 0.4, which is the same as that of Comparative Example 1, it was confirmed that the laminated films of Examples 1 to 4 each maintain a transparency equivalent to that of Comparative Example 1. As summarized in Table 1, the laminated films of Examples 7 and 10 each achieved a low haze value. Since each of the coating liquids of Examples 1 to 4, 7, and 10 showed a superior storage stability, it was confirmed that a laminated film of stable quality can be produced efficiently in Examples 1 to 4, 7, and 10. Comparative Example 2, in which the intermediate layer was not formed as in Comparative Example 1 and a photobase generator was not used, achieved a low refractive index and a low haze but was very poor in peel strength. Thus, Comparative Example 2 had a difficulty in continuous production as a rolled product and had no practical applicability.

INDUSTRIAL APPLICABILITY

As described above, the present invention can provide an optical laminate, a method of producing an optical laminate, an optical element, an image display, a method of producing an optical element, and a method of producing an image display that achieve a superior film strength and a property that a void-provided layer and a pressure-sensitive adhesive/adhesive layer are not easily peeled from each other. Owing to the aforementioned properties, the optical laminate of the present invention easily achieves a low refractive index, which can be a substitute for an air layer, for example. Thus, there is no need to provide air layers by disposing components at regular spacings for achieving a low refractive index. By disposing the optical laminate of the present invention at a desired site, a low refractive index can be imparted. Thus, the optical laminate of the present invention is useful for an optical element which requires a low refractive index, for example. The optical laminate of the present invention may be used for an optical element and an image display of the present invention, for example. The present invention, however, is not limited thereto and can be used for any purpose.

EXPLANATION OF REFERENCE NUMERALS

-   10 base -   20 void-provided layer -   20′ coating film (after drying) -   20″ sol particle liquid -   21 void-provided layer with improved strength -   101 delivery roller -   102 coating roller -   110 oven zone -   111 hot air fan (heating unit) -   120 chemical treatment zone -   121 lamp (light irradiation unit) or hot air fan (heating unit) -   130 a pressure-sensitive adhesive/adhesive layer applying zone -   130 intermediate forming zone -   131 a pressure-sensitive adhesive/adhesive layer applying unit -   131 hot air fan (heating unit) -   105 winding roller -   106 roll -   201 delivery roller -   202 liquid reservoir -   203 doctor (doctor knife) -   204 micro-gravure -   210 oven zone -   211 heating unit -   220 chemical treatment zone -   221 light irradiation unit or heating unit -   230 a pressure-sensitive adhesive/adhesive layer applying zone -   230 intermediate forming zone -   231 a pressure-sensitive adhesive/adhesive layer applying unit -   231 hot air fan (heating unit) -   251 winding roller 

1. An optical laminate comprising: a void-provided layer; an intermediate layer; and a pressure-sensitive adhesive/adhesive layer, wherein the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked in this order, and the intermediate layer is formed by forming the pressure-sensitive adhesive/adhesive layer on the void-provided layer.
 2. The optical laminate according to claim 1, wherein the void-provided layer has a thickness in a range from 0.01 μm to 1000 μm.
 3. The optical laminate according to claim 1, wherein the intermediate layer has a thickness in a range from 0.001 μm to 10 μm.
 4. The optical laminate according to claim 1, wherein the void-provided layer has a refractive index of 1.25 or less.
 5. The optical laminate according to claim 1, wherein the thickness of the intermediate layer is less than the thickness of the void-provided layer.
 6. The optical laminate according to claim 1, wherein the void-provided layer has a proportion of void space of 40 vol % or more.
 7. The optical laminate according to claim 1, wherein the void-provided layer has a haze value of less than 5%.
 8. The optical laminate according to claim 1, wherein the void-provided layer includes a part where one kind or two or more kinds of structural units that form a structure with minute void spaces are chemically bonded, and the void-provided layer contains a crosslinking assisting agent for indirectly bonding the structural units.
 9. The optical laminate according to claim 8, wherein a content of the crosslinking assisting agent in the void-provided layer relative to a weight of the structural unit is in a range from 0.01 wt % to 20 wt %.
 10. The optical laminate according to claim 1, further comprising: a resin film, wherein the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on the resin firm in this order.
 11. The optical laminate according to claim 10, wherein the resin film is a long resin film, and the laminated film is a long laminated film roll.
 12. A method of producing an optical laminate in which a void-provided layer, an intermediate layer, and a pressure-sensitive adhesive/adhesive layer are stacked in this order, comprising steps of: forming the void-provided layer; forming the pressure-sensitive adhesive/adhesive layer on the void-provided layer; and forming the intermediate layer.
 13. The method according to claim 12, wherein the optical laminate is an optical laminate in which the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on a resin film in this order, and the void-provided layer is formed on the resin film in the void-provided layer forming step.
 14. The method according to claim 12, wherein the intermediate layer is formed by heating the void-provided layer and the pressure-sensitive adhesive/adhesive layer in the intermediate layer forming step.
 15. The method according to claim 12, further comprising a step of: forming a void-provided structure which is a precursor of the void-provided layer prior to the void-provided layer forming step, wherein the precursor contains a substance that generates a strength improver that improves a strength of the void-provided layer, the substance is a substance that generates the strength improver by light irradiation or heating, the substance does not generate the strength improver in the precursor forming step, and the substance generates the strength improver by light irradiation or heating in at least one of the void-provided layer forming step and the intermediate layer forming step.
 16. The method according to claim 15, wherein the strength improver contains an acid or a basic substance.
 17. The method according to claim 12, wherein a refractive index of the void-provided layer after formation of the intermediate layer is 0.1 more than a refractive index of the void-provided layer before the formation of the intermediate layer.
 18. The method according to claim 12, wherein the void-provided layer is formed so as to have a refractive index of 1.25 or less.
 19. The method according to claim 12, wherein the void-provided layer is formed so as to have a proportion of void space of 40 vol % or more.
 20. The method according to claim 12, wherein the void-provided layer is formed so as to have a thickness in a range from 0.01 μm to 100 μm.
 21. The method according to claim 12, wherein the void-provided layer is formed so as to have a haze value of less than 5%.
 22. The method according to claim 12, further comprising a step of: causing a crosslinking reaction in the void-provided layer.
 23. The method according to claim 22, wherein the crosslinking reaction step is a strength improving step of improving a strength of the void-provided layer.
 24. The method according to claim 22, wherein the optical laminate is an optical laminate in which the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on a resin film in this order, the void-provided layer is formed on the resin film in the void-provided layer forming step, and the crosslinking reaction step is a step of improving a peel strength of the void-provided layer to the resin film.
 25. The method according to claim 22, wherein the intermediate layer forming step also serves as the crosslinking reaction step.
 26. The method according to claim 12, wherein the void-provided layer is formed by indirectly bonding one kind or two or more kinds of structural units that form a structure with minute void spaces using a crosslinking assisting agent in the void-provided layer forming step.
 27. The method according to claim 26, wherein an amount of the crosslinking assisting agent to be added relative to a weight of the structural unit is in a range from 0.01 wt % to 20 wt %.
 28. The method according to claim 12, wherein the optical laminate is an optical laminate in which the void-provided layer, the intermediate layer, and the pressure-sensitive adhesive/adhesive layer are stacked on a long resin film in this order, the void-provided layer is continuously formed on the long resin film in the void-provided layer forming step, and the pressure-sensitive adhesive/adhesive layer is continuously formed on the void-provided layer in the pressure-sensitive adhesive/adhesive layer forming step.
 29. An optical element comprising: the optical laminate according to claim
 1. 30. An image display comprising: the optical element according to claim
 29. 